- Polymer Property : Flexural Yield Strength = 181 MPa
Polymer Property : Flexural Yield Strength = 181 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 181 - 181 MPa @Temperature 232 - 232 °C |
26300 - 26300 psi @Temperature 450 - 450 °F |
Average value: 181 MPa Grade Count:1 |
| Overview of materials for Polyamide-Imide, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyamide-Imide, Glass Filled". Each property range of values reported is minimum and maximum values of .. |
|||
| Flexural Yield Strength | 181 MPa @Thickness 3.20 mm |
26300 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical Lupox® GP2300R PBT+GF30% Description: Injection Molding, PBT+GF30%, Anti-HydrolysisApplication: E&E (Speed Nut & Body)CAS No. 65997-17-3 and 24968-12-5Information provided by LG Chemical |
|||
| Flexural Yield Strength | 181 MPa @Thickness 3.20 mm |
26300 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical Lupox® SG5300 PBT+PET+GF30% Description: Injection Molding, PBT+PET+GF30%, Good Surface Application: E&E, Automotive (Switch)CAS No. 65997-17-3, 24968-12-5 and 25038-59-9Information provided by LG Chemical |
|||
| Flexural Yield Strength | 181 MPa | 26300 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Noryl PX7446 PPE+PS This data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Yield Strength | 181 MPa | 26300 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP WFL36 PBT (Europe-Africa-Middle East) LNP* Lubricomp* WFL36 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE. |
|||
| Flexural Yield Strength | 181 MPa | 26300 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP DF004 PC (Europe-Africa-Middle East) LNP* THERMOCOMP* DF004 is a compound based on Polycarbonate resin containing Glass Fiber. |
|||
| Flexural Yield Strength | 181 MPa | 26300 psi | ASTM D790 |
| Cheng Yu Plastic ML3435 PC, 35% Glass Fiber |
|||
| Flexural Yield Strength | 181 MPa | 26300 psi | ASTM D790 |
| Cheng Yu Plastic T883GV25 Flame Retardant PBT, 25% Glass Fiber |
|||
| Flexural Yield Strength | 181 MPa | 26300 psi | ASTM D790 |
| Cheng Yu Plastic T889G25 PBT, 25% Glass Fiber |
|||
| Flexural Yield Strength | 181 MPa | 26300 psi | ASTM D790 |
| Cheng Yu Plastic FV30730 POM, 30% Mineral Reinforced |
|||