Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 4005 SI Polyphthalamide (PPA) Glass Fiber 30% - Silicone
(discontinued **) Glass Fiber 30% - SiliconeComments:Glass FiberSilicone LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information pro.. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 2299 X 68910 A Polyetheretherketone (PEEK) Long Glass Fiber 40%
(discontin Long Glass Fiber 40%Comments:Long Glass FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 1110 Polyethylene Terephthalate (PET) Glass Fiber 55%
(discontinued **)< Glass Fiber 55%Comments:Glass FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for .. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 1185 Polyethylene Terephthalate (PET) Carbon Fiber 30%
(discontinued **)&l Carbon Fiber 30%Comments:Carbon FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data fo.. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
Solvay Specialty Polymers Kadel® E-1230 Polyketone
(discontinued **) Electrical Conductor. High performance proprietary semi-crystalline polymer based resins with exceptional solvent resistance and high temperature performance. They provide strength and stiffness, p.. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 2185 TFE 5 Polyetherimide (PEI) Carbon Fiber 30% - PTFE 5%
(discontinued * Carbon Fiber 30% - PTFE 5%Comments:Carbon FiberPTFE LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provid.. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 2185 TFE 13 SI 2 Polyetherimide (PEI) Carbon Fiber 30% - PTFE 13% - Silicone 2%
& Carbon Fiber 30% - PTFE 13% - Silicone 2%Comments:Carbon FiberPTFE LubricatedSilicone LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can af.. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 209D Nylon 6/12 (PA 6/12) Glass Fiber 50%
(discontinued **) Glass Fiber 50%Comments:Glass FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for .. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
Techmer ES Electrafil® J-1/CF/30/TF/13/SI/2 Nylon 66, 30% Carbon Fiber, 13% PTFE, 2% Silicone |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
Techmer ES HiFill® PPS GF40 TL13 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: PTFE LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
Techmer ES Plastiblend® PA6 GF30 RM BK Nylon 6 Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightProcessing Method: Injection MoldingInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | Long Beam, dry |
Hexcel® HexPly® F522 Epoxy Resin, W3C282 Carbon Fabric Hexcel designation: TW3C282-42"-F522; Fiber: Toho® G30/500-3KInformation provided by HexCel |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
Clariant Renol PEEKSP0002 Polyetheretherketone, 30% Glass Fiber Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 284C Nylon 11 (PA 11) Carbon Fiber 25%
(discontinued **) Carbon Fiber 25%Comments:Carbon FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data fo.. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 285D TFE 13 SI 2 Nylon 6/12 (PA 6/12) Carbon Fiber 30% - PTFE 13% - Silicone 2%
& Carbon Fiber 30% - PTFE 13% - Silicone 2%Comments:Carbon FiberPTFE LubricatedSilicone LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can af.. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
PolyOne Edgetek® NI-30CF/000 Nylon 6/10 - 30% Carbon Fiber Reinforced
(discontinued **) Data provided by PolyOne. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 208B Nylon 6/10 (PA 6/10) Glass Fiber 45%
(discontinued **) Glass Fiber 45%Comments:Glass FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for .. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 285B TFE 13 SI 2 Nylon 6/10 (PA 6/10) Carbon Fiber 30% - PTFE 13% - Silicone 2%
& Carbon Fiber 30% - PTFE 13% - Silicone 2%Comments:Carbon FiberPTFE LubricatedSilicone LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can af.. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 209E Amorphous Nylon (Am. PA) Glass Fiber 50%
(discontinued **) Glass Fiber 50%Comments:Glass FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for .. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 3999X56542B Polyetherketoneetherketoneketone (PEKEKK), Wear Resistant
(discontinued **) Data is for injection molded specimens and was provided by the manufacturer, RTP Company.This product has been discontinued, please contact RTP Company regarding alternate grades. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 283E Amorphous Nylon (Am. PA) Carbon Fiber 20%
(discontinued **) Carbon Fiber 20%Comments:Carbon FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data fo.. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 1389 HEC Polyphenylene Sulfide (PPS) Nickel-Coated Carbon Fiber 50% - EMI/ESD
&n Nickel-Coated Carbon Fiber 50% - EMI/ESDComments:EMI/RFI/ESD ProtectionNickel-Coated Carbon FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can a.. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 4082A Polyphthalamide - Hot Water Mold (PPA) Carbon Fiber 15%
(discontinue Carbon Fiber 15%Comments:Carbon FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data fo.. |
|||
Flexural Yield Strength | 276 - 303 MPa | 40000 - 44000 psi | Average value: 290 MPa Grade Count:3 |
Overview of materials for Polyethylene Terephthalate (PET), 60% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 60% Glass Reinforced". Specific grades with glass content between 55% .. |
|||
Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
RTP Company RTP 4008A FR Polyphthalamide - Hot Water Mold (PPA) Electronic Encapsulation - 45% Glass Fiber - Flame Retardant Electronic Encapsulation - 45% Glass Fiber - Flame RetardantComments:Encapsulation GradeGlass FiberFlame RetardantUnless otherwise specified, all data listed is for natural or black colored material.. |