- Polymer Property : Flexural Yield Strength = 31300 psi
Polymer Property : Flexural Yield Strength = 31300 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 216 MPa | 31300 psi | DIN 53455; ASTM D790 |
| Kolon SPESIN® KP213G45 Flame Retardant PBT Resin
(discontinued **) SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High hea.. |
|||
| Flexural Yield Strength | 216 MPa | 31300 psi | DIN 53455; ASTM D790 |
| Kolon SPESIN® KP2122G30VO G/F Reinforced & Retardant PBT Resin
(discontinued **) SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High hea.. |
|||
| Flexural Yield Strength | 216 - 425 MPa | 31300 - 61600 psi | Average value: 326 MPa Grade Count:106 |
| Overview of materials for Nylon 66, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. .. |
|||
| Flexural Yield Strength | 216 MPa @Thickness 6.40 mm |
31300 psi @Thickness 0.252 in |
3mm/min; ASTM D790 |
| LG Chemical LUMID GP2200A(W) PA6+GF20%, General Purpose Feature: Injection Molding, PA6+MF23%, High ImpactPA6+GF20%, General PurposeApplication: HMID, SLMP B, HolderCAS No. 32131-17-2 and 65997-17-3Information provided by LG Chemical |
|||
| Flexural Yield Strength | 216 MPa @Thickness 3.20 mm |
31300 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUMID GP2251BF PA66+GF25%, Flame Retardant Feature: Injection Molding, PA66+GF25%, Flame RetardantApplication: IT/OA (Micro Switch)CAS No. 32131-17-2, 65997-17-3, 88497-56-7, 1309-64-4 and 138265-88-0Information provided by LG Chemical |
|||
| Flexural Yield Strength | 216 MPa | 31300 psi | DIN 53455; ASTM D790 |
| Kolon SPESIN® KP513G30WBL Multi Reinforced PBT Resin SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High.. |
|||
| Flexural Yield Strength | 216 MPa | 31300 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN133G20 G/F Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Flexural Yield Strength | 216 MPa | 31300 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® T101G36 PET, 36% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 216 MPa | 31300 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® C501G40 Nylon 6, 40% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 216 MPa | 31300 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® T101G36 PET, 36% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 216 MPa | 31300 psi | ASTM D790 |
| Toyobo Vylopet® EMC330K Glass Reinforced Polyester, Easy Molding Grade HB UL-94 classApplications: General and high rigidity componentsGeneral features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and tracking resistance, c.. |
|||
| Flexural Yield Strength | 216 MPa | 31300 psi | ASTM D790 |
| Cheng Yu Plastic N6GV15 Flame Retardant Nylon 6, 15% Glass Filled |
|||
| Flexural Yield Strength | 216 MPa | 31300 psi | ASTM D790 |
| Cheng Yu Plastic FR200GV45 Flame Retardant Nylon 66, 45% Glass Fiber |
|||
| Flexural Yield Strength | 216 MPa | 31300 psi | ASTM D790 |
| A. Schulman ComAlloy E-16674B PPS, Electrically Conductive - Carbon Fiber Filled Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Flexural Yield Strength | 216 MPa | 31300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics LNP Verton PV007SV_YW8D151 PA 6 Preliminary data for 35% long fiber single pellet color filled PA6This data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Yield Strength | 216 MPa | 31300 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® C501G40 Nylon 6, 40% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||