Polymer Property : Flexural Yield Strength = 5660 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	39.0 MPa	5660 psi	ASTM D790
Nylene® 609 Nylon 6, 50% RH, Film/Extrusion Grade Film Grade. Nylene 609 is a high viscosity, extrusion resin recommended for practically all types of extrusion including profile, film, and extrusion coating. It is especially recommended for fl..
Flexural Yield Strength	39.0 MPa	5660 psi	ASTM D790
North Wood Plastics Polypropylene with 60% Wood Fiber, Molding Grade Data provided by North Wood Plastics, Inc.
Flexural Yield Strength	39.0 MPa	5660 psi	ASTM D790
Rotuba MH Cellulose Acetate Property values at 50% RH.Data provided by the manufacturer.
Flexural Yield Strength	39.0 - 106 MPa	5660 - 15400 psi	Average value: 80.3 MPa Grade Count:65
Overview of materials for Polystyrene, Heat Resistant Grade This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Heat Resistant Grade". Each property range of values reported is minimum and maximum values..
Flexural Yield Strength	39.0 MPa	5660 psi	ASTM D790
Ineos Nova 5751 High Impact Polystyrene (discontinued **) High flow, Good impact, USP Class VIApplications: Single service impact, Medical, Housewares, CompoundingProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwi..
Flexural Yield Strength	39.0 MPa	5660 psi	2 mm/min; ASTM D790
Solvay Specialty Polymers Solef® 1015/0078 PVDF Homopolymer (discontinued **) Key features of this grade: Plasticized, Offshore, Piping, Formulated. Recommended processing is extrusion. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorina..
Flexural Yield Strength	39.0 - 276 MPa	5660 - 40000 psi	Average value: 101 MPa Grade Count:94
Overview of materials for Nylon 66, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum ..
Flexural Yield Strength	39.0 MPa	5660 psi	ASTM D790
Tipco Tipcolene® FPT 30 BK CP - 30% Talc Polypropylene Homopolymer, Special Heat Stability 30% Talc Reinforced PP Homopolymer with Special AdditivesApplications: AutomotivesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Flexural Yield Strength	39.0 MPa	5660 psi	ASTM D790
Covestro Baydur® 726 IBS Polyurethane Structural Foam RIM, Density 40 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. IBS = Interactive Blowing System RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience ..
Flexural Yield Strength	39.0 MPa	5660 psi	ASTM D790
Covestro Baydur® STR/F-375 Polyurethane Composite SRIM Foam, 20% Glass Filled, MDI-based 2-Component Liquid System Contains continuous strand fiberglass mat.0.125 in. thickness.Information provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer ..