Polymer Property : Tensile Strength, Ultimate = 1250 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1250 MPa @Temperature -196 °C	181000 psi @Temperature -321 °F	EN min; EN 10002-5
Outokumpu 4301 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll..
Tensile Strength, Ultimate	1250 MPa @Temperature -196 °C	181000 psi @Temperature -321 °F	EN min; EN 10002-5
Outokumpu 4311 Cr-Ni Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms..
Tensile Strength, Ultimate	>= 1250 MPa	>= 181000 psi
Kobe Steel KS15-5-3 Beta Titanium Alloy, AMS 4914, Solution treated and aged, Forgings Nominal Composition: Ti-15 Mo-5 Zr-3 AlApplications: Implant materials for orthopedics, erosion shields, gold club heads. Features:Super high strength.Information provided by Kobe Steel
Tensile Strength, Ultimate	1250 MPa	182000 psi
International Mold Steel NAK55 Precipitation Hardened Mold Steel Description: NAK55 is a precipitation, or age-hardened mold steel with a through hardness of approximately 40 HRc. NAK55 is ideal for use in plastic and rubber molds and other applications where imp..
Tensile Strength, Ultimate	1250 MPa	181000 psi
Industeel SuperplastÂ® 400 High Hardness Mold Steel SUPERPLASTÂ® 400 is an injection plastic mold steel pre-hardened to a high level of hardness. It is delivered at a typical hardness of 125 kg/mm2. This steel is specially adapted for heavy-duty ..
Tensile Strength, Ultimate	1250 MPa	181000 psi
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370Â°C (700Â°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	1250 MPa	181000 psi	hardness of 40 HRC
Bohler-Uddeholm UDDEHOLM QRO® 90 SUPREME Hot Work Tool Steel Chromium-molybdenum-vanadium alloyed steelQRO® 90 SUPREME is a premium hot work die steel with high hot yield strength and very good temper resistance. Especially suited for die casting of aluminum..
Tensile Strength, Ultimate	1250 MPa @Temperature 23.0 °C	181000 psi @Temperature 73.4 °F
Assab Steels QRO 90 SUPREME Hot Work Steel QRO 90 SUPREME is a high-performance, chromium-molybdenum-vanadium alloyed hot-work tool steel which is characterized by: Excellent high temperature strength and hot hardnessVery good temper resista..
Tensile Strength, Ultimate	1250 - 1300 MPa	182000 - 189000 psi
Latrobe Lescalloy® Jethete M-152 ESR 6" RCS High Strength Stainless Steel LESCALLOY JETHETE M-152 ESR is a nitrogen bearing, hardenable 12% chromium stainless steel intended for various structural components requiring high strength and good oxidation resistance up to 800°..