Polymer Property : Tensile Strength, Ultimate = 181000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1250 MPa @Temperature -196 °C	181000 psi @Temperature -321 °F	EN min; EN 10002-5
Outokumpu 4301 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll..
Tensile Strength, Ultimate	1250 MPa @Temperature -196 °C	181000 psi @Temperature -321 °F	EN min; EN 10002-5
Outokumpu 4311 Cr-Ni Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms..
Tensile Strength, Ultimate	>= 1250 MPa	>= 181000 psi
Kobe Steel KS15-5-3 Beta Titanium Alloy, AMS 4914, Solution treated and aged, Forgings Nominal Composition: Ti-15 Mo-5 Zr-3 AlApplications: Implant materials for orthopedics, erosion shields, gold club heads. Features:Super high strength.Information provided by Kobe Steel
Tensile Strength, Ultimate	1250 MPa	181000 psi
Industeel SuperplastÂ® 400 High Hardness Mold Steel SUPERPLASTÂ® 400 is an injection plastic mold steel pre-hardened to a high level of hardness. It is delivered at a typical hardness of 125 kg/mm2. This steel is specially adapted for heavy-duty ..
Tensile Strength, Ultimate	1250 MPa	181000 psi
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370Â°C (700Â°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	1250 MPa	181000 psi	hardness of 40 HRC
Bohler-Uddeholm UDDEHOLM QRO® 90 SUPREME Hot Work Tool Steel Chromium-molybdenum-vanadium alloyed steelQRO® 90 SUPREME is a premium hot work die steel with high hot yield strength and very good temper resistance. Especially suited for die casting of aluminum..
Tensile Strength, Ultimate	1248 MPa	181000 psi
Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 732°C (1350°F)/8hr/AC to 621°C (1150°F)/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t..
Tensile Strength, Ultimate	1250 MPa @Temperature 23.0 °C	181000 psi @Temperature 73.4 °F
Assab Steels QRO 90 SUPREME Hot Work Steel QRO 90 SUPREME is a high-performance, chromium-molybdenum-vanadium alloyed hot-work tool steel which is characterized by: Excellent high temperature strength and hot hardnessVery good temper resista..
Tensile Strength, Ultimate	1248 MPa	181000 psi
Carpenter Gall-Tough® Stainless, Annealed and Cold Drawn Bar, 20% Cold Work Data provided by Carpenter Technology Corporation.Threshold Galling Stress 103 MPa (higher stress tests not performed). The avg. total volume loss on the wear test is 5 mm³ at 100 rpm.Gall-Tough®..
Tensile Strength, Ultimate	1248 MPa	181000 psi	Hardened at 1850°F for 30 min, oil quenched and tempered for 4 hrs at 500°F [9.5 mm plate, transverse]
AK Steel 410 Cb Martensitic Stainless steel AK Steel 410 Cb is an improved version of standard Type 410. The addition of columbium offers 3 major advantages: 1) Greater ease in heat treating, 2) Higher strength and toughness, 3) Improved gra..
Tensile Strength, Ultimate	1248 MPa @Treatment Temp. 649 °C, Time 3.60e+6 sec	181000 psi @Treatment Temp. 1200 °F, Time 1000 hour	Room temp test after thermal exposure
Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b..