Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | |
Mykroy/Mycalex MM 400 Machining Grade Glass-bonded Mica Composite Natural mica filler. Does not burn. Good radiation resistance (3 x 10^10 Rads-Cobalt).This ceramoplastic material is a versatile and efficient insulating material designed to meet the exacting dem.. |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | |
Mykroy/Mycalex MM 500 Machining Grade Glass-bonded Mica Composite Synthetic mica filler. Does not burn. Better radiation resistance (3 x 10^10 Rads-Cobalt) than grade 400.This ceramoplastic material is a versatile and efficient insulating material designed to me.. |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | ASTM D412 |
5286 Polyurethane-based Biomedical Elastomer |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | ASTM D412 |
5370 Polyurethane-based Biomedical Elastomer |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Lubri-Tech™ PS-15GB/15T Polybutylene Terephthalate (PBT), Glass Bead Filled, PTFE Lubricated
(discont Description/Features:Glass Bead FilledPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Ultimate | 41.4 - 95.0 MPa | 6000 - 13800 psi | Average value: 75.7 MPa Grade Count:19 |
Overview of materials for Polyphenylene Ether, 10% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 10% Glass Filled". Specific grades with glass content between 5% and 14% are includ.. |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | ASTM D638-95 |
Multibase Multi-ABS 3832 Natural Multi-ABS 3832 is specially formulated for ease of processability, controllability, and thin-walled parts where higher than normal temperatures are being used. This product also shows higher than n.. |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | ASTM Data |
Styron Magnum™ 341 ABS, Low Gloss MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM .. |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | |
Elastomer Engineering E700-70 Polyurethane An extremely tough polyester-based urethane with excellent shock absorbing quality and resistance to abrasion and chemicals. Typical uses: shock deadening pads, abrasion resistant liners and pads, .. |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | ASTM D412 |
Lubrizol Estane® ALR PC85A Thermoplastic Polyurethane Type: Estane® ALR PC85A is a polycarbonate diol based thermoplastic polyurethane (TPU).Features: Hydrolytically stable, very durableAvailable in Americas, Europe, Middle East, Africa, India and Asi.. |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | ASTM D638 |
Ecomass® 1080TU95 Tungsten Filled Polyamide Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applications.High Specific GravityTungsten Powder Filled Polyamide (PA) AlloyExcellent ToughnessInformation provided b.. |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | ASTM D638 |
Ecomass® 1080ZD94 Tungsten Filled Polyamide Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applications.High Specific GravityTungsten Filled Polyamide (PA) AlloyExcellent ToughnessInformation provided by Techn.. |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | |
Dymax 9-984-B Conformal Coating High Performance Light-Curing Adhesives and Coatings for Electronic AssemblyDymax 9-984-B Conformal CoatingCures to an opaque black finish; hides components or circuitry from view; protects sensitiv.. |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | ETFE film property; ASTM D638 |
Arlon 25188T010 Silicone Rubber/Laminated ETFE Film Liner: 3 mil PTFE coated fiberglass; Side 1: uncured silicone rubber; Substrate: laminated ETFE film, treated for adhesion |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | ETFE film property; ASTM D638 |
Arlon 25188T017 Silicone Rubber/Laminated ETFE Film Liner: 3 mil PTFE coated fiberglass; Side 1: uncured silicone rubber; Substrate: laminated ETFE film, treated for adhesion |
|||
Tensile Strength, Ultimate | 41.4 - 55.2 MPa | 6000 - 8000 psi | |
Bulk Molding Compounds BMC 605LS Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 605LS molding compound is a low-shrink, mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is characterized by good mol.. |
|||
Tensile Strength, Ultimate | 41.4 - 55.2 MPa | 6000 - 8000 psi | |
Bulk Molding Compounds BMC 800 Thermoset Polyester, Corrosion Resistant BMC 800 compounds are UL rated 94V0/5V. These compounds exhibit excellent strength, corrosion and weather resistant properties. As with all other BMCI compounds, this Series can be supplied in logs,.. |
|||
Tensile Strength, Ultimate | 41.4 - 48.3 MPa | 6000 - 7000 psi | |
Bulk Molding Compounds BMC 1423 Wear Resistant, Electrical Grade BMC 1423 is a wear-resistant electrical grade material used in applications where there are moving parts. Best anti-wear properties are exhibited when used in conjunction with mating parts molded fr.. |
|||
Tensile Strength, Ultimate | 41.4 - 55.2 MPa | 6000 - 8000 psi | |
Bulk Molding Compounds BMC 610 Mineral Filled, Glass Reinforced Polyester Compound BMC 610 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is set a part form other medium impact el.. |
|||
Tensile Strength, Ultimate | 41.4 - 51.7 MPa | 6000 - 7500 psi | |
Bulk Molding Compounds BMC 945 Conductive Grade Bulk Molding Compound BMC 945 is an ESD level Conductive grade of Bulk Molding Compound and is suitable for compression, transfer and stuffer injection molding. It is characterized by excellent flow and controlled reacti.. |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | |
Dymax 3086 Solvent-Free Plastic Adhesive Solvent-Free Adhesives for Plastic Assembly in SecondsDymax® Light-Weld® and Ultra 3000 Series UV and UV/Visible Curing Adhesives for plastic assembly provide instant durable bonds to cure a wide .. |
|||
Tensile Strength, Ultimate | 41.4 - 64.0 MPa | 6000 - 9280 psi | Average value: 53.1 MPa Grade Count:22 |
Overview of materials for Acetal Homopolymer, PTFE-Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, PTFE-Filled". Each property range of values reported is minimum and maximum values o.. |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | TM R050-36 |
Resinlab® EP1285HD-14 Highly Filled, Medium Viscosity Casting Resin Resinlab™ EP1285 (Formerly Lab Product W021901 series) is a highly filled, medium viscosity black casting resin designed for applications requiring a high degree of thermal conductivity and a low C.. |
|||
Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | ASTM D412 |
Dow PELLETHANE® 2355-55DE Polyurethane Elastomer, Polyester Polyadipate Based
(discontinued **) Description: PELLETHANE® 2355-55DE polyester polyadipate based polyurethane elastomer has excellent oil and chemical resistance. Applications include: Film, Sheet, Tubing, Recreation and sporting e.. |