Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 655 MPa | 95000 psi | |
Pacific Sintered Materials F-244-S(HT) High Carbon Steel Powdered Metal Applications:Highly stressed mechanical componentsGood hardenabilityEquivalent MPIF Specification: F-0008-85(HT)All information provided by Pacific Sintered Metals. |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Bar, Cold Drawn High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Bar, Cold Drawn High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Tensile Strength, Ultimate | 655 - 790 MPa | 95000 - 115000 psi | |
Materion Beryllium Copper Alloy 174 Strip; 1/2HT (TH02) Temper (UNS C17410) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 95%Stress Relaxation after 1000 hrs @ 200°C: 67%Formability Ratio, 90° Bend, R.. |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | |
Materion BrushBronze® 95510 (AMS 4880) Centrifugal Cast 1.0" - 17.0" Information supplied by Brush Wellman Engineered Materials.BrushBronze™ 95510 is an Aluminum-Nickel-Bronze alloy that combines high strength, ductility, and good abrasion resistance under sever.. |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | |
Materion BrushBronze® 95510 (AMS 4880) Continuous Cast 4.0" - 17.0" Information supplied by Brush Wellman Engineered Materials.BrushBronze™ 95510 is an Aluminum-Nickel-Bronze alloy that combines high strength, ductility, and good abrasion resistance under sever.. |
|||
Tensile Strength, Ultimate | 655 - 724 MPa | 95000 - 105000 psi | |
Materion BrushCAST® 165C High Strength Casting Alloy (As Cast & Aged) Pouring Temperature: 1010-1120°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescr.. |
|||
Tensile Strength, Ultimate | 655 - 724 MPa | 95000 - 105000 psi | |
Materion BrushCAST® 165CT Fine Grain Casting Alloy (As Cast & Aged) Pouring Temperature: 1010-1120°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescr.. |
|||
Tensile Strength, Ultimate | 655 - 724 MPa | 95000 - 105000 psi | |
Materion BrushCAST® 275C High Strength Casting Alloy (As Cast & Aged) Pouring Temperature: 960-1035°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescri.. |
|||
Tensile Strength, Ultimate | 655 - 724 MPa | 95000 - 105000 psi | |
Materion BrushCAST® 275CT Fine Grain Casting Alloy (As Cast & Aged) Pouring Temperature: 960-1035°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescri.. |
|||
Tensile Strength, Ultimate | >= 655 MPa | >= 95000 psi | |
MetalTek ESCOLOY 45D® Cast UNS J93345 Duplex Stainless Steel Excellent seawater corrosion resistance combined with nearly twice the strength of common stainless steels. Produced under license of ESCO Corp.Applications: Offshore piping systems, couplings. Cent.. |
|||
Tensile Strength, Ultimate | 655 - 896 MPa | 95000 - 130000 psi | |
Materion Beryllium Nickel Strip - Alloy 360 Annealed Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: as suppliedFormability Ratio, 90° Bend, Radius/Thickness (Good Way): 0Formability Ratio (bad Way): .. |
|||
Tensile Strength, Ultimate | 655 MPa @Temperature 427 °C |
95000 psi @Temperature 801 °F |
|
Haynes Hastelloy® C-22® alloy, 0.71-3.2 mm thick sheet, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Tensile Strength, Ultimate | 655 MPa @Temperature 93.0 °C |
95000 psi @Temperature 199 °F |
|
Haynes Hastelloy® G-30® alloy, plate and bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | Annealed |
Special Metals INCONEL® Alloy 600 A nickel-chromium alloy with good oxidation resistance at high temperatures and resistance to chloride-ion stress-corrosion cracking, corrosion by high-purity water, and caustic corrosion. Used for.. |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | 0° Fiber Direction |
Saint-Gobain Quartzel® Fabric/Cyanate Ester Resin Composite Fiber: Quartzel® 8 Harness Fabric Style 581. Resin 954-2A System.Quartzel® fiber is produced from quartz crystal that is ground, purified, fiberized by a fusion process. It is homogeneous, n.. |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | |
Universal Wire Works 310 Stainless Steel Electrode Universal 310 electrodes were developed for the welding of 310 stainless steel. The deposited weld metal exhibits the same chemical analysis and oxidation resistance as the 310 base metal. Maintenan.. |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | |
Universal Wire Works 321 Stainless Steel (AMS 5689) Filler Metal Universal 321 is a titanium-stabilized filler metal used with the gas metal arc and gas tungsten arc processes. Universal 321 stabilized weldments are often subjected to severe corrosive and high te.. |
|||
Tensile Strength, Ultimate | 655 - 717 MPa | 95000 - 104000 psi | |
Eagle Brass 260 Cartridge Brass, Extra Spring Alloy C260 is commonly used for electrical components, electronic parts, and mechanical fasteners. The alloy has good strength but poor stress relaxation characteristics and does not make a particul.. |
|||
Tensile Strength, Ultimate | 655 - 758 MPa | 95000 - 110000 psi | |
Eagle Brass 510 Phosphor Bronzes 5% A, Spring Alloy C510 is an alloy with good strength, formability and stress relaxation characteristics, and solderability. Applications include electronic parts, springs, switches, contacts and fasteners.Info.. |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | |
Crucible Steel 420 and 420F Chromium Steel Crucible 416 Plus is a hardenable chromium steel which is the general purpose cutlery grade. This grade is magnetic in all conditions. Information provided by Crucible Specialty Metals. |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | Castings |
CMW® 100 Copper Alloy CMW® 100 material is a heat treatable, high strength, high conductivity copper base alloy. Its properties are a combination of highest strength and hardness with relatively high electrical and ther.. |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | |
ATI Allegheny Ludlum AL 29-4C® Stainless Steel, UNS S44735 AL 29-4C alloy is a superferritic stainless steel designed by Allegheny Ludlum for extreme resistance to chloride ion pitting, crevice corrosion and stress corrosion cracking, as well as general cor.. |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | |
ATI Allvac® Nickelvac® 690 UNS N06690 Nickel Superalloy Uses: Nuclear, mineral acids manufacturing and processing facilities, high-temperature gas-phase reactors.Property values are for samples in the metallurgical condition: 1825°F anneal.Information p.. |
|||
Tensile Strength, Ultimate | 655 MPa @Temperature 93.0 °C |
95000 psi @Temperature 199 °F |
|
ATI Allegheny Ludlum AL 2003™ Duplex Stainless Steel Characteristics: superior stress corrosion cracking resistance to Types 316 and 317, yield strength double that of conventional austenitic stainless steel, good corrosion resistance, good chloride s.. |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | |
ATI Allegheny Ludlum Altemp® 263 Nickel-Based alloy Characteristics: high strength up to 1500°F, oxidation resistance up to 2000°FInformation provided by Allegheny Ludlum |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | |
ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 302, 0% Cold Rolled (UNS S30200) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
Tensile Strength, Ultimate | 655 MPa | 95000 psi | Hardened at 1850°F for 30 min, oil quenched and tempered for 4 hrs at 1400°F [9.5 mm plate, transverse] |
AK Steel 410 Cb Martensitic Stainless steel AK Steel 410 Cb is an improved version of standard Type 410. The addition of columbium offers 3 major advantages: 1) Greater ease in heat treating, 2) Higher strength and toughness, 3) Improved gra.. |
|||
Tensile Strength, Ultimate | 655 MPa @Temperature 316 °C |
95000 psi @Temperature 601 °F |
|
Haynes Hastelloy® C-22® alloy, 6.4-19.1 mm thick plate, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |