Polymer Property : Tensile Strength, Ultimate = 9720 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	67.0 MPa	9720 psi	ASTM D638
Plaskolite Optix® CA-81 General Purpose Acrylic Resin Extrusion Grade Pellets. Highest Molecular weight.
Tensile Strength, Ultimate	67.0 MPa	9720 psi	ASTM D638
Plaskolite West Optix® CA-81 General Purpose Acrylic Resin Extrusion Grade Pellets. Highest Molecular weight.
Tensile Strength, Ultimate	67.0 MPa	9720 psi	5 mm/min
Polimeri Europa KOSTIL B266 Styrene Acrylonitrile Symbol according to ISO 1043-1: SAN Grade designation according to ISO 4894-SAN 2,M,105-15 Standard injection moulding grade with good chemical resistance Application fields: household and small ..
Tensile Strength, Ultimate	67.0 MPa	9720 psi
Polycasa Acryl® G 66 Acrylic, Injection Molding Grade Injection molding grade used for: Fresnel lenses, filter screens for TVs and VDUs, drawing instruments.Data was collected by ISO methods.Quinn Manufacturing Group rebranded its Plastics Division as ..
Tensile Strength, Ultimate	67.0 MPa	9720 psi	5 mm/min; parallel to flow; ASTM D638
Asahi Kasei Tenac® 2013A Acetal Homopolymer, UV Stabilized (discontinued **) Similar to 3013A, but higher in molecular weight.Applications: Pipe fittings, rollers, exterior automotive parts.This product is not a part of the standard product line dated 2003.
Tensile Strength, Ultimate	67.0 MPa	9720 psi	5 mm/min (0.2 in/min)
Aardvark Polymers AARTELÂ® 2100UV Acetal Homopolymer Rotational Molding Resin Aartel 2100UV is a natural acetal homopolymer with UV stabilizers.Aartel 2100UV is a medium viscosity resin with excellent flow characteristics.Aartel 2100UV is available in natural white and may be..
Tensile Strength, Ultimate	67.0 MPa	9720 psi
Lucite International LuciteÂ® 30B Acrylic Bead Resin LuciteÂ® 30B is usually compression molded and is a high flow methyl methacrylate copolymer.General LuciteÂ® Acrylic Bead Resin Information: Used in casting and embedment, compression molding, d..
Tensile Strength, Ultimate	67.0 MPa	9720 psi	cond; ISO 527-1/-2
DSM Novamid® 1013GMF H2 NAT/BK37 PA6-GF30 30% Glass Reinforced, Heat Stabilized, Injection Molding, Excellent Dimensional Stability
Tensile Strength, Ultimate	67.0 MPa	9720 psi	5 mm/min
Arkema Group Orgalloy® RS 66M25 Nylon 66 Alloy, 25% Mineral Filled (Conditioned) RS 66 series, rigid polyamide 66 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional propertie..
Tensile Strength, Ultimate	67.0 MPa	9720 psi	5mm/min; ISO 527
BASF Ultramid® 8267G HS BK-102 15/25% Glass/Mineral Filled PA6 (Conditioned) Ultramid 8267G HS BK-102 is a heat stabilized, black pigmented, 40% mineral and glass fiber reinforced nylon 6 injection molding compound. It possesses a balance of engineering properties in combin..
Tensile Strength, Ultimate	67.0 MPa	9720 psi	ATSM D638
Ashley Polymers Ashlene® P292 PPO Extrusion grade, highest heat deflection temperature and good impact strength.Data provided by the manufacturer
Tensile Strength, Ultimate	67.0 MPa	9720 psi	ASTM D638
A. Schulman ComAlloy Hiloy® 119 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.30% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate	67.0 MPa @Thickness 2.00 mm	9720 psi @Thickness 0.0787 in	molded plaque, cured 20 hr at 100°C; ASTM D412
BASF Elastollan® C85A10 (917) Wire & Cable Grade Polyurethane Elastomer As with all TPU products this grade must be dried prior to processing.Information provided by BASF Corporation.
Tensile Strength, Ultimate	67.0 MPa @Temperature 120 °C	9720 psi @Temperature 248 °F	ISO 527
LATI LASULF G/20 20% Glass Reinforced Polysulfone (PSU) (Unverified Data**) Description: Lasulf products are composed of polysulfone (PSU). They feature good thermal and mechanical properties such as excellent toughness, even at low temperatures, excellent dimensional stabi..
Tensile Strength, Ultimate	67.0 MPa	9720 psi	ISO 527
LATI LARIL 13-V1 Polyphenylene Oxide (PPOm) (UL94V-1) (discontinued **) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most ..
Tensile Strength, Ultimate	67.0 MPa	9720 psi	5mm/min; ISO 527
BASF Ultramid® SEGM35 H1 BK-126 15/25% Glass/Mineral Filled PA6 (Conditioned) Ultramid SEGM35 H1 BK-126 is a 40% glass/mineral reinforced injection molding grade. It offers enhanced surface appearance, it also exhibits similar UV weathering characteristics compared to 8267G ..