BASF Ultramid® 8267G HS BK-102 15/25% Glass/Mineral Filled PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8267G HS BK-102 15/25% Glass/Mineral Filled PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8267G HS BK-102 is a heat stabilized, black pigmented, 40% mineral and glass fiber reinforced nylon 6 injection molding compound. It possesses a balance of engineering properties in combination with excellent dimensional stability, low warp and resistance to sink-mark formation. It exhibits high strength, rigidity, and good heat distortion temperature. It resists creep under load and the heat stabilizer system extends its retention of properties at elevated temperatures. It has good chemical resistance to greases, oils and hydrocarbons.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
dry; ISO 1183
Water Absorption 0.90 %
0.90 %
24 hour; ISO Test
5.7 %
5.7 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 1.6 %
1.6 %
beginning dry (23°C/50% R.H.); ISO 62
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength at Break 67.0 MPa
9720 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 67.0 MPa
9720 psi
5mm/min; ISO 527
Elongation at Break 14 %
14 %
5mm/min; ISO 527
14 %
14 %
0.2 in/min; ASTM Test
Tensile Modulus 4.16 GPa
603 ksi
1mm/min; ISO 527
Flexural Strength 90.0 MPa
13100 psi
ISO Data
Flexural Modulus 3.68 GPa
534 ksi
ISO Data
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Processing Properties Metric English Comments
Melt Temperature 275 °C
527 °F
Injection molding
Mold Temperature 95.0 °C
203 °F
Injection molding
Descriptive Properties Value Comments
Color BK-102
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes