Polymer Property : Shear Strength = 93.1 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	93.1 MPa	13500 psi	ASTM D732
Solvay Specialty Polymers KetaSpire® KT-820 GF30 Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-820 GF30 is a medium flow, 30% glass fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire..
Shear Strength	93.1 MPa @Thickness 15.7 mm	13500 psi @Thickness 0.620 in	ASTM D732
Industrial Laminates/Norplex NP313 Cotton Fabric Description: Canvas phenolic laminate with molybdenum disulfide lubricant. Mechanical properties slightly lower than NP310.Thickness Tested: 0.062", 0.125" & 0.500"
Shear Strength	93.1 MPa @Thickness 15.7 mm	13500 psi @Thickness 0.620 in	ASTM D732
Industrial Laminates/Norplex NP320 Cotton Fabric Description: Fine weave (less than 4 ounce/square yard) cotton fabric commonly called linen, combined with phenolic resin to provide better machining than NP310. For smaller and more intricate shape..
Shear Strength	93.1 MPa @Thickness 15.7 mm	13500 psi @Thickness 0.620 in	ASTM D732
Industrial Laminates/Norplex NP320E Cotton Fabric Description: Similar to NP320 with improved moisture resistance. Suitable for electrical applications in moderate humidity conditions.Thickness Tested: 0.062", 0.125", and 0.500â€
Shear Strength	93.1 MPa @Thickness 15.7 mm	13500 psi @Thickness 0.620 in	ASTM D732
Industrial Laminates/Norplex NP347 Cotton Fabric Description: Bleached canvas with high temperature phenolic resin with molybdenum disulfide lubricant. Low moisture absorption. Capable of 150Â°C continuous operation.Thickness Tested: 0.062", 0.1..
Shear Strength	93.1 MPa	13500 psi	ASTM D732
Solvay Specialty Polymers KetaSpireÂ® KT-820 GF30 Polyetheretherketone (PEEK), 30% Glass Fiber KetaSpireÂ® KT-820 GF30 is a medium flow, 30% glass fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaS..
Shear Strength	93.1 MPa	13500 psi	Ultimate
Ensinger TECAPEI® 20% Glass Reinforced, made from Ultem® 2200 PEI TECAPEI™ is an amorphous thermoplastic polyetherimide (PEI) made from Sabic Innovative Plastics' Ultem® 1000 and 2000 series resins. The unreinforced 1000 series materials are translucent amber in..