Polymer Property : Tensile Creep Modulus, 1000 hours = 400 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Creep Modulus, 1000 hours	400 - 1450 MPa	58000 - 210000 psi	Average value: 1160 MPa Grade Count:40
Overview of materials for Acetal Copolymer, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Unreinforced". Each property range of values reported is minimum and maximum values of..
Tensile Creep Modulus, 1000 hours	400 - 840 MPa	58000 - 122000 psi	Average value: 663 MPa Grade Count:3
Overview of materials for Nylon 66, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Impact Grade". Each property range of values reported is minimum and maximum values of appropr..
Tensile Creep Modulus, 1000 hours	400 MPa	58000 psi
LyondellBasell LupolenÂ® 6031 M HDPE, Injection Molding Grade Easy flow, injection molding grade for fruit crates, tote boxes and bottle crates, cartridges, protective headgear, buckets, dishes, cartridges for adhesive film canisters, aerosol lids, child seats..
Tensile Creep Modulus, 1000 hours	400 MPa	58000 psi	At 1% Deformation; DIN 53444
Wolf Kunststoff ZEDEX® ZX-100EL55 A1F Polymer Alloy, Elastomer Modified Main Characteristics: Rubbery; Soft; High shock absorption; High impact resistance; Elongation > 300%Applications: Handling, Vessel and Pump, Steel and Water, Chemical Engineering, Automitve Technol..
Tensile Creep Modulus, 1000 hours	400 MPa	58000 psi	23°C; ISO 899; DIN 53444
Zell-Metall Engineering Plastics Zellamid 250 (PA6.6) at 50% RH Zellamid® 250 is noted for its high temperature resistance and high tensile strength. It is the hardest and most rigid type of extruded Nylon. Main characteristics are high resistance to fuels, oil..
Tensile Creep Modulus, 1000 hours	400 MPa	58000 psi	ISO 899-1
BASF Ultraform® N2650 Z6 (LEV) POM Description: Is a POM + PUR, elastomer-modified injection-molding grade for applications requiring the highest impact strength together with low stiffness.Information provided by BASF
Tensile Creep Modulus, 1000 hours	400 - 1050 MPa	58000 - 152000 psi	Average value: 845 MPa Grade Count:16
Overview of materials for Acetal Copolymer, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Impact Modified". Each property range of values reported is minimum and maximum values..