Polymer Property : Flexural Modulus = 331 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
PolyOne Geon™ Vinyl Rigid Molding M3900 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
PolyOne LubriOne™ PC-000/05T-2S Polycarbonate (PC) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Flexural Modulus	2.28 GPa	331 ksi	ISO 178
PolyOne OnFlex™ BIO 5180D-E0014 Thermoplastic Elastomer (TPE) OnFlex™ BIO 5100 series thermoplastic elastomer compounds are glass reinforced thermoplastic polyurethane compounds made from renewable natural sources. These compounds contain at least 20% renewab..
Flexural Modulus	2.28 GPa	331 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Cycoloy® LG9020 PC+ABS Low Gloss Cycoloy. Available only in natural, to be custom color concentrated and UV stabilized at the molding press.
Flexural Modulus	2.28 GPa @Thickness 3.17 mm	331 ksi @Thickness 0.125 in	ASTM D790
PTS Tristar® PC-10R-(V15) 15 MFI UV Stabilized Polycarbonate With Release Information provided by Polymer Technology and Services, LLC (PTS).
Flexural Modulus	2.28 GPa	331 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® HFD1930 PC Copolymer 55 MFR LEXAN High Flow Ductile Copolymer, Natural color only
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DL002F PC LNP LUBRICOMP* DL002F is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Internally Lubricated, Superior Molding.
Flexural Modulus	2.28 GPa	331 ksi	Conditioned; ASTM D790
Solvay Specialty Polymers Amodel® AT-1002 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AT-1002 HS is a neat, toughened, heat stabilized polyphthalamide (PPA) resin that offers superior retention of properties after humid thermal aging; high impact at low temperature and better ..
Flexural Modulus	2.28 GPa	331 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® HFD1910 PC Copolymer 55 MFR LEXAN High Flow Ductile Copolymer, Natural colors only
Flexural Modulus	2.28 GPa	331 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® HFD1910 PC Copolymer (Asia Pacific) 55 MFR LEXAN High Flow Ductile Copolymer, Natural colors only
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
Covestro Apec® DP9-9333 High-Heat Polycarbonate, General Purpose, UV-Stabilized (discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ..
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
Covestro Apec® DP9-9341 High-Heat Polycarbonate, General Purpose (discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ..
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
Covestro Apec® DP9-9343 High-Heat Polycarbonate, UV Stabilized (discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ..
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
Covestro Apec® DP9-9351 High-Heat Polycarbonate, General Purpose (discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ..
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
Covestro Apec® DP9-9354 High-Heat Polycarbonate, Flame-Retardant (discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ..
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
Covestro Apec® DP9-9373 High-Heat Polycarbonate, General Purpose, UV-Stabilized (discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ..
Flexural Modulus	2.28 GPa	331 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP COLORCOMP DX98735H PC LNP* COLORCOMP* DX98735H is an unfilled Polycarbonate resin. Added feature of this grade is: Healthcare.
Flexural Modulus	2.28 GPa	331 ksi	2mm/min; ASTM D790
Kingfa PC-WT01 Weather Resistance PC Features:Excellent balance propertiesGood weather resistanceHigh impact strengthGood electro-plating propertiesGood processing propertiesApplications:Injection moldingAutomobile instrument panelElec..
Flexural Modulus	2.28 GPa	331 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP KI001XXJ Acetal LNP* LUBRICOMP* KI001XXJ is a compound based on Acetal containing 2% Silicone. Added features of this grade include: Wear Resistant, Healthcare.
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
SABIC Innovative Plastics LNP LUBRILOY D20009 PC LNP LUBRILOY* D20009 is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Flame Retardant, Wear Resistant.
Flexural Modulus	2.28 GPa @Temperature 23.0 Â°C	331 ksi @Temperature 73.4 Â°F	ISO 178
Solvay Specialty Polymers AmodelÂ® AT-1002 HS Polyphthalamide (PPA) AmodelÂ® AT-1002 HS is a neat, toughened, heat stabilized polyphthalamide (PPA) resin that offers superior retention of properties after humid thermal aging; high impact at low temperature and bet..
Flexural Modulus	2.28 GPa	331 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON CD0001 PS LNP* STAT-KON* CD000I is a compound based on Polystyrene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact.
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
Videolar 825 High Impact Polystyrene (HIPS) Injection molding gradeMedium melt flow and high glossGood balance between rigidity and impactFeatures: Excellent mechanical strengthExcellent temperature resistancehigh impactApplications: Toys, ap..
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
Covestro Makrolon® 3258 Polycarbonate, General Purpose, Mold Release, Biocompatibility It is the responsibility of the medical device, biological product, or pharmaceutical manufacturer (Manufacturer) to determine the suitability of all component parts and raw materials, including the..
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
Covestro Makrolon® 6255 Polycarbonate, Flame Retardant, High Productivity, Mold Release Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Flexural Modulus	2.28 - 10.7 GPa	331 - 1550 ksi	Average value: 5.47 GPa Grade Count:98
Overview of materials for Polycarbonate, Glass + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Glass + PTFE Filled". Each property range of values reported is minimum and maximum value..
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
Covestro Apec® DP9-9353 High-Heat Polycarbonate, UV Stabilized (discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ..
Flexural Modulus	2.28 GPa	331 ksi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Xylex HX7409HP PC+POLYESTER (Asia Pacific) Low flow, polycarbonate/Polyester alloy; contains mold release. For medical devices and pharmaceutical applications. Healthcare management of change (MoC), biocompatible (ISO 10993 or USP Class VI)..
Flexural Modulus	2.28 GPa @Temperature 175 °C	331 ksi @Temperature 347 °F	ISO 178
Solvay Specialty Polymers Amodel® A-1565 HS Polyphthalamide (PPA) (Unverified Data**) Amodel A-1565 HS is a 65% glass and mineral-reinforced polyphthalamide (PPA) designed to be cost-effective in applications requiring high stiffness, good dimensional stability and good retention of ..
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
Solvay Specialty Polymers Amodel® ET-1000 HS Polyphthalamide (PPA) (Unverified Data**) Amodel ET-1000 HS is an impact modified, heat stabilized polyphthalamide (PPA) that exhibits exceptional impact strength and toughness. Like all Amodel PPA resins, ET-1000 HS offers high fatigue str..