Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Glass + PTFE Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.28 - 1.61 g/cc
0.0462 - 0.0582 lb/in³
Average value: 1.43 g/cc Grade Count:102
Filler Content 10.0 - 40.0 %
10.0 - 40.0 %
Average value: 20.3 % Grade Count:44
Water Absorption 0.0170 - 0.250 %
0.0170 - 0.250 %
Average value: 0.123 % Grade Count:62
Additive Loading 15.0 - 30.0 %
15.0 - 30.0 %
Average value: 20.8 % Grade Count:6
Linear Mold Shrinkage 0.000500 - 0.00800 cm/cm
0.000500 - 0.00800 in/in
Average value: 0.00313 cm/cm Grade Count:101
Linear Mold Shrinkage, Transverse 0.00400 - 0.00700 cm/cm
0.00400 - 0.00700 in/in
Average value: 0.00529 cm/cm Grade Count:7
Melt Flow 3.00 - 22.2 g/10 min
3.00 - 22.2 g/10 min
Average value: 12.0 g/10 min Grade Count:8
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90.0 - 95.0
90.0 - 95.0
Average value: 92.3 Grade Count:3
Hardness, Rockwell R 114 - 120
114 - 120
Average value: 118 Grade Count:25
Tensile Strength, Ultimate 27.6 - 124 MPa
4000 - 18000 psi
Average value: 83.6 MPa Grade Count:99
Tensile Strength, Yield 0.539 - 117 MPa
78.2 - 17000 psi
Average value: 61.4 MPa Grade Count:12
Elongation at Break 1.00 - 120 %
1.00 - 120 %
Average value: 5.52 % Grade Count:79
Elongation at Yield 1.80 - 7.00 %
1.80 - 7.00 %
Average value: 3.54 % Grade Count:17
Modulus of Elasticity 2.41 - 13.8 GPa
350 - 2000 ksi
Average value: 6.03 GPa Grade Count:86
Flexural Yield Strength 39.3 - 193 MPa
5700 - 28000 psi
Average value: 132 MPa Grade Count:100
Flexural Modulus 2.28 - 10.7 GPa
331 - 1550 ksi
Average value: 5.47 GPa Grade Count:98
Compressive Yield Strength 72.4 - 110 MPa
10500 - 16000 psi
Average value: 92.2 MPa Grade Count:8
Izod Impact, Notched 0.320 - 12.3 J/cm
0.600 - 23.0 ft-lb/in
Average value: 1.73 J/cm Grade Count:89
Izod Impact, Unnotched 0.801 - 16.0 J/cm
1.50 - 30.0 ft-lb/in
Average value: 7.99 J/cm Grade Count:66
Izod Impact, Notched (ISO) 9.50 - 17.9 kJ/m²
4.52 - 8.52 ft-lb/in²
Average value: 12.8 kJ/m² Grade Count:5
Izod Impact, Unnotched (ISO) 34.4 - 58.1 kJ/m²
16.4 - 27.6 ft-lb/in²
Average value: 43.5 kJ/m² Grade Count:5
Charpy Impact Unnotched 2.70 - 6.00 J/cm²
12.8 - 28.6 ft-lb/in²
Average value: 3.82 J/cm² Grade Count:12
2.00 - 3.70 J/cm²

@Temperature -30.0 - -30.0 °C
9.52 - 17.6 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 2.97 J/cm² Grade Count:7
Charpy Impact, Notched 0.800 - 2.50 J/cm²
3.81 - 11.9 ft-lb/in²
Average value: 1.72 J/cm² Grade Count:6
2.00 - 2.00 J/cm²

@Temperature -30.0 - -30.0 °C
9.52 - 9.52 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 2.00 J/cm² Grade Count:2
Falling Dart Impact 11.6 - 18.4 J
8.56 - 13.6 ft-lb
Average value: 15.9 J Grade Count:6
Coefficient of Friction 0.150 - 0.550
0.150 - 0.550
Average value: 0.281 Grade Count:11
Coefficient of Friction, Static 0.120 - 0.480
0.120 - 0.480
Average value: 0.225 Grade Count:11
K (wear) Factor 15.0 - 254 x 10-8 mm³/N-M
7.45 - 126 x 10-10 in³-min/ft-lb-hr
Average value: 108 x 10<sup>-8</sup> mm³/N-M Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 23.4 - 58.0 µm/m-°C
13.0 - 32.2 µin/in-°F
Average value: 36.3 µm/m-°C Grade Count:19
Thermal Conductivity 0.202 - 0.317 W/m-K
1.40 - 2.20 BTU-in/hr-ft²-°F
Average value: 0.283 W/m-K Grade Count:15
Maximum Service Temperature, Air 130 - 150 °C
266 - 302 °F
Average value: 140 °C Grade Count:12
Deflection Temperature at 0.46 MPa (66 psi) 136 - 149 °C
277 - 300 °F
Average value: 145 °C Grade Count:46
Deflection Temperature at 1.8 MPa (264 psi) 121 - 152 °C
250 - 306 °F
Average value: 140 °C Grade Count:73
Vicat Softening Point 150 - 170 °C
302 - 338 °F
Average value: 161 °C Grade Count:10
Flammability, UL94 HB - 5VA
HB - 5VA
Grade Count:73
Electrical Properties Metric English Comments
Electrical Resistivity 1000 - 1.00e+16 ohm-cm
1000 - 1.00e+16 ohm-cm
Average value: 7.38e+15 ohm-cm Grade Count:53
Surface Resistance 1000 - 1.00e+16 ohm
1000 - 1.00e+16 ohm
Average value: 7.72e+14 ohm Grade Count:13
Insulation Resistance 1.00e+12 ohm
1.00e+12 ohm
Average value: 1.00e+12 ohm Grade Count:10
Dielectric Constant 3.20 - 3.40
3.20 - 3.40
Average value: 3.34 Grade Count:5
Dielectric Strength 17.7 - 18.1 kV/mm
450 - 460 kV/in
Average value: 17.9 kV/mm Grade Count:5
Dissipation Factor 0.00700 - 0.0100
0.00700 - 0.0100
Average value: 0.00780 Grade Count:5
Arc Resistance 120 sec
120 sec
Average value: 120 sec Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 249 - 299 °C
480 - 570 °F
Average value: 280 °C Grade Count:34
Nozzle Temperature 282 - 310 °C
540 - 590 °F
Average value: 299 °C Grade Count:13
Melt Temperature 221 - 338 °C
430 - 640 °F
Average value: 302 °C Grade Count:70
Mold Temperature 65.6 - 121 °C
150 - 250 °F
Average value: 96.4 °C Grade Count:90
Drying Temperature 110 - 130 °C
230 - 266 °F
Average value: 121 °C Grade Count:67
Moisture Content 0.0200 %
0.0200 %
Average value: 0.0200 % Grade Count:42
Dew Point -28.9 °C
-20.0 °F
Average value: -28.9 °C Grade Count:35
Injection Pressure 41.4 - 138 MPa
6000 - 20000 psi
Average value: 86.8 MPa Grade Count:57