Solvay Specialty Polymers Amodel® ET-1000 HS Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® ET-1000 HS Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel ET-1000 HS is an impact modified, heat stabilized polyphthalamide (PPA) that exhibits exceptional impact strength and toughness. Like all Amodel PPA resins, ET-1000 HS offers high fatigue strength, good chemical resistance and high mechanical property retention over a broad temperature and humidity range. - Natural: ET-1000 HS NTData is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183/A
Water Absorption 0.70 %

@Time 86400 sec
0.70 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.015 cm/cm
0.015 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
R-Scale; ASTM D785
Tensile Strength at Break 60.0 MPa

@Temperature 23.0 °C
8700 psi

@Temperature 73.4 °F
ISO 527-2
Tensile Strength 62.7 MPa

@Temperature 23.0 °C
9090 psi

@Temperature 73.4 °F
Conditioned; ASTM D638
68.9 MPa

@Temperature 23.0 °C
9990 psi

@Temperature 73.4 °F
ASTM D638
96.5 MPa

@Temperature -40.0 °C
14000 psi

@Temperature -40.0 °F
Conditioned; ASTM D638
110 MPa

@Temperature -40.0 °C
16000 psi

@Temperature -40.0 °F
ASTM D638
Tensile Strength, Yield 33.8 MPa

@Temperature 100 °C
4900 psi

@Temperature 212 °F
ISO 527-2
70.3 MPa

@Temperature 23.0 °C
10200 psi

@Temperature 73.4 °F
ISO 527-2
Elongation at Break 7.0 %

@Temperature 23.0 °C
7.0 %

@Temperature 73.4 °F
ISO 527-2
11 %

@Temperature -40.0 °C
11 %

@Temperature -40.0 °F
Conditioned; ASTM D638
12 %

@Temperature -40.0 °C
12 %

@Temperature -40.0 °F
ASTM D638
18 %

@Temperature 23.0 °C
18 %

@Temperature 73.4 °F
Conditioned; ASTM D638
20 %

@Temperature 23.0 °C
20 %

@Temperature 73.4 °F
ASTM D638
95 %

@Temperature 100 °C
95 %

@Temperature 212 °F
ISO 527-2
Elongation at Yield 4.3 %

@Temperature 100 °C
4.3 %

@Temperature 212 °F
ISO 527-2
5.0 %

@Temperature 23.0 °C
5.0 %

@Temperature 73.4 °F
ISO 527-2
6.0 %

@Temperature 23.0 °C
6.0 %

@Temperature 73.4 °F
Conditioned; ASTM D638
6.0 %

@Temperature 23.0 °C
6.0 %

@Temperature 73.4 °F
ASTM D638
9.0 %

@Temperature -40.0 °C
9.0 %

@Temperature -40.0 °F
Conditioned; ASTM D638
9.0 %

@Temperature -40.0 °C
9.0 %

@Temperature -40.0 °F
ASTM D638
Tensile Modulus 2.41 GPa
350 ksi
Conditioned; ASTM D638
2.41 GPa
350 ksi
ASTM D638
2.00 GPa

@Temperature 100 °C
290 ksi

@Temperature 212 °F
ISO 527-2
2.41 GPa

@Temperature 23.0 °C
350 ksi

@Temperature 73.4 °F
ISO 527-2
Flexural Strength 85.5 MPa
12400 psi
Conditioned; ASTM D790
109 MPa
15800 psi
ASTM D790
44.1 MPa

@Temperature 100 °C
6400 psi

@Temperature 212 °F
ISO 178
70.3 MPa

@Temperature 23.0 °C
10200 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 2.14 GPa
310 ksi
ASTM D790
2.28 GPa
331 ksi
ASTM D790
1.31 GPa

@Temperature 100 °C
190 ksi

@Temperature 212 °F
ISO 178
1.79 GPa

@Temperature 23.0 °C
260 ksi

@Temperature 73.4 °F
ISO 178
Shear Strength 58.6 MPa
8500 psi
ASTM D732
Izod Impact, Notched 1.10 J/cm

@Temperature -40.0 °C
2.06 ft-lb/in

@Temperature -40.0 °F
ASTM D256
9.10 J/cm

@Temperature 23.0 °C
17.0 ft-lb/in

@Temperature 73.4 °F
ASTM D256
11.0 J/cm

@Temperature 23.0 °C
20.6 ft-lb/in

@Temperature 73.4 °F
Conditioned; ASTM D256
Izod Impact, Notched (ISO) 73.0 kJ/m²
34.7 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched NB
NB
ISO 179/1eU
Charpy Impact, Notched 7.80 J/cm²
37.1 ft-lb/in²
ISO 179/1eA
Dart Drop, Total Energy 54.2 J
40.0 ft-lb
ASTM D3763
Taber Abrasion, mg/1000 Cycles 6.0

@Load 1.00 kg
6.0

@Load 2.20 lb
CS-17 Wheel; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 77.0 µm/m-°C

@Temperature 0.000 - 100 °C
42.8 µin/in-°F

@Temperature 32.0 - 212 °F
TMA; ASTM E831
140 µm/m-°C

@Temperature 100 - 200 °C
77.8 µin/in-°F

@Temperature 212 - 392 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 81.0 µm/m-°C

@Temperature 0.000 - 100 °C
45.0 µin/in-°F

@Temperature 32.0 - 212 °F
ASTM E831
110 µm/m-°C

@Temperature 100 - 200 °C
61.1 µin/in-°F

@Temperature 212 - 392 °F
ASTM E831
Melting Point 310 °C
590 °F
Peak; ASTM D3418
310 °C
590 °F
ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi) 109 °C
228 °F
Unannealed; ISO 75-2/A
120 °C
248 °F
Annealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 304 - 318 °C
579 - 604 °F
Front Barrel Temperature 316 - 329 °C
601 - 624 °F
Melt Temperature 321 - 343 °C
610 - 649 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 110 °C
230 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.045 %
0.045 %
Descriptive Properties Value Comments
Additive Heat Stabilizer
Impact Modifier
Appearance Natural Color
Automotive Specifications ASTM D4000 PA1234 Color: BK684 Black
ASTM D4000 PA1234 Color: NT Natural
ASTM D6779 PA1234
DELPHI 23295267 Color: BK-684, NT Black & Natural
DELPHI 28213409 Color: BK-684, NT Black & Natural
DELPHI M-2965 Color: BK684 Black
DELPHI M-2965 Color: NT Natural
DELPHI MSP24103175 Color: NT Natural
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Ductile
Good Chemical Resistance
Heat Stabilized
Hot Water Moldability
Impact Modified
Low Warpage
Forms Pellets
Generic PPA
Processing Method Water-Heated Mold Injection Molding
RoHS Compliance RoHS Compliant
Uses Automotive Applications
Automotive Electronics
Automotive Under the Hood
Connectors
General Purpose
Housings
Industrial Applications
Industrial Parts
Lawn and Garden Equipment
Machine/Mechanical Parts
Metal Replacement
Copyright © lookpolymers.com All Rights Reserved