Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 1.96 GPa | 284 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® EXL1036 PC Copolymer Lexan* EXL1036 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high viscosity grade designed for (co-)extrusion. This resin offers extreme low temperature (-60 C) ductility and good h.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® EXL1036 PC Copolymer (Asia Pacific) Lexan* EXL1036 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high viscosity grade designed for (co-)extrusion. This resin offers extreme low temperature (-60 C) ductility and good h.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® EXL1036 PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1036 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high viscosity grade designed for (co-)extrusion. This resin offers extreme low temperature (-60 C) ductility and good h.. |
|||
Flexural Modulus | 1.96 - 3.10 GPa | 284 - 450 ksi | Average value: 2.32 GPa Grade Count:33 |
Overview of materials for Polycarbonate, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Extruded". Each property range of values reported is minimum and maximum values of approp.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
Hyosung Topilene J301CP PP J301CP Injection Special Purpose GradeApplications: Cap of pressure bottleCharacteristics:High stiffnessSlip propertyInformation provided by Hyosung Corporation |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | DIN 53452; ASTM D790 |
Kolon KOPA® KN177N Nylon Extrusion Resin Excellent transparent & flexible copolyamide, typical applications are fishing nets & fishing linesInformation provided by US distributor, API-Kolon. |
|||
Flexural Modulus | 1.96 GPa @Thickness 6.40 mm |
284 ksi @Thickness 0.252 in |
5mm/min; ASTM D790 |
LG Chemical Lupox® TE5000GU PBT+PC Description: Injection Molding, PBT+PC, High Impact, Dimensional Stability, Good WeatherabilityApplication: Automotive (Door Garnish, Door Handle)CAS No. 137050-02-03, 24968-12-5 and 103598-77-2Info.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
LG Chemical LUPOY HR-5007AX Heat Resistant PC/ABS Alloy, Unreinforced Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive.. |
|||
Flexural Modulus | 1.96 GPa @Thickness 3.20 mm |
284 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical SH610S ABS, Excellent Surface, High Impact Feature: Extrusion Molding, Excellent Surface, High ImpactApplication: Bag, miscellaneousCAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 1% secant; ASTM D790-02 |
Ipiranga Petrochem PH 0321 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
KKPC Kuhmo HF400 Flame Retarded General Purpose HIPS Key features: Translucent Injection. Common Uses: TV and VCR housing.HIPS is a functional resin made by copolymerization of styrene monomer and PBR. It shows excellent balance between impact-resista.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SD-0150AT ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SV-0167 ABS, Unreinforced Extrusion Grade Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® TX-0520T TRABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® WR-9100 ASA, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® CF-1051 PC, Unreinforced High Impact High-impact material for the exterior material of mobile phoneInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SV-0167 ABS, Unreinforced Extrusion Grade Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® WX-9700 ASA, Unreinforced Extrusion Grade Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
Samyang Trirex® 3030I Polycarbonate TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, elec.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
Samyang Trirex® 3030U Polycarbonate, UV Stabilized TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, elec.. |
|||
Flexural Modulus | 1.96 GPa @Thickness 3.20 mm |
284 ksi @Thickness 0.126 in |
ASTM D790 |
Supreme Petrochem SP 6460 High Heat Polystyrene Characteristics High impact and modulus Easy flow High heat resistance & strength Available in any dark colorProcessing Injection moldingApplications Instrument enclosures Automobile interior pa.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1902HU Talc Fortified Polypropylene DescriptionPolyfort® FPP 1902 HU is a 10% talc fortified polypropylene. It exhibits high flow and is stabilized for UV resistance. Information provided by A. Schulman. |
|||
Flexural Modulus | 1.96 GPa @Thickness 6.40 mm |
284 ksi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IM-17 A EP ABS Electro Plating Applications Electroplating & Hot Stamping GradesInformation provided by Bhansali |
|||
Flexural Modulus | 1.96 GPa @Thickness 6.40 mm |
284 ksi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron SE32H Extrusion ABS Very High Impact, Better Flow and Sheet/Pipe/Profile applicationInformation provided by Bhansali |
|||
Flexural Modulus | 1.96 GPa @Thickness 6.40 mm |
284 ksi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IM-17 A EP ABS Electro Plating Applications Electroplating & Hot Stamping GradesInformation provided by Bhansali |
|||
Flexural Modulus | 1.96 GPa @Thickness 6.40 mm |
284 ksi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron SE32H Extrusion ABS Very High Impact, Better Flow and Sheet/Pipe/Profile applicationInformation provided by Bhansali |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
Tipco Tipcolene® ISL 10 BX1 - 10% Talc/Mineral Reinforced Polypropylene Homopolymer, High Flow, Stiffness & Impact Strength 10% Mineral Reinforced, High Stiffness, High Impact PP HomopolymerApplications: Automotive InteriorsProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
Indi.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® EG-0763 ABS, Unreinforced Good chemical resistanceInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
Samyang Trirex® 3026B Polycarbonate PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3026B is an extrusion grade.Applications: BottlesInformation provided by Samyang. |
|||
Flexural Modulus | 1.96 GPa @Thickness 3.20 mm |
284 ksi @Thickness 0.126 in |
ASTM D790 |
Supreme Petrochem SP 731 9920 High Impact Polystyrene Characteristics Speciality grade containing silicon oil to provide wear resistance and high opacity jet black color Easy flowing grade Processing Injection moldingApplications Camera parts Photogr.. |