Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.410 GPa | 59.5 ksi | method 1, Proc.B; ASTM D-790 |
Multibase Multi-Flex® TPE G 7680 BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Flexural Modulus | 0.410 GPa | 59.5 ksi | ISO 178 |
Solvay Engineered Polymers DEXFLEX® E756 TPO
(discontinued **) Description: DEXFLEX® E756 thermoplastic olefinic elastomer (TPO) is designed for extruded automotive air-bag covers. This material provides excellent rigidity, durability and low-temperature toug.. |
|||
Flexural Modulus | 0.410 - 0.410 GPa @Temperature 90.0 - 90.0 °C |
59.5 - 59.5 ksi @Temperature 194 - 194 °F |
Average value: 0.410 GPa Grade Count:1 |
Overview of materials for Polypropylene, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Molded". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Flexural Modulus | 0.410 GPa | 59.5 ksi | ASTM D790 |
UBE UBESTA® 3030JFX1 Plasticized Industrial Grade Nylon 12 Description: UBE UBESTA® Industrial grade Nylon 12Comments: UV resistance, heat resistanceInformation provided by UBE. |
|||
Flexural Modulus | 0.410 GPa | 59.5 ksi | ASTM D790 |
UBE UBESTA® 3030JI5L Plasticized Automotive Grade Nylon 12 Description: UBE UBESTA® Automotive grade Nylon 12Comments: meet SAE J844, DIN73378 HIPHLInformation provided by UBE. |
|||
Flexural Modulus | 0.410 GPa | 59.5 ksi | ASTM D790 |
UBE UBESTA® 3030JLX1 Plasticized Automotive Grade Nylon 12 Description: UBE UBESTA® Automotive grade Nylon 12Comments: UV resistance, heat resistanceInformation provided by UBE. |
|||
Flexural Modulus | 0.410 GPa | 59.5 ksi | ASTM D790 |
Chevron Phillips Marlex® 7104 LLDPE Sheet Extrusion Resin Type: Hexene CopolymerCharacteristics: Outstanding ESCRGood melt strengthExcellent flexibilityGood processabilityGood glossHigh COFApplications: Landfill coversFlat and round-die productsCoext.. |