Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 19.3 MPa @Temperature 37.8 °C |
2800 psi @Temperature 100 °F |
ASTM D732 |
Greene Tweed Avalon® 16 PTFE, Glass, Molybdenum Filled Products made from Avalon® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin.. |
|||
Shear Strength | 19.3 MPa @Temperature 26.7 °C |
2800 psi @Temperature 80.0 °F |
ASTM D732 |
Greene Tweed Avalon® 9 PTFE, Graphite Filled Products made from Avalon® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin.. |
|||
Shear Strength | 19.3 MPa @Temperature 60.0 °C |
2800 psi @Temperature 140 °F |
Lap Shear |
Hexcel® Redux® 335K Adhesive film for bonding metallic and composite components (0.03 psf) Redux 335 is a film adhesive curing at 250F. It is available in a range of standard areal weights from 0.015 to 0.06 psf. It is available either unsupported or with knitted and/or matt carrier for a.. |
|||
Shear Strength | 19.3 MPa @Temperature 21.1 °C |
2800 psi @Temperature 70.0 °F |
Tensile Lap Shear; Aluminum No Primer; ASTM D1002 |
Hexcel® Redux® HP655 Toughened BMI film Adhesive Redux® HP655 is a toughened BMI structural adhesive designed for metal to metal, composite to composite, and honeycomb sandwich bonding for both co-cured and precured composite skins. Redux® HP655.. |
|||
Shear Strength | 19.3 MPa @Temperature 21.1 °C |
2800 psi @Temperature 70.0 °F |
Tensile Lap Shear; Composite; ASTM D1002 |
Hexcel® Redux® HP655 Toughened BMI film Adhesive Redux® HP655 is a toughened BMI structural adhesive designed for metal to metal, composite to composite, and honeycomb sandwich bonding for both co-cured and precured composite skins. Redux® HP655.. |
|||
Shear Strength | 19.3 MPa @Temperature -53.0 °C |
2800 psi @Temperature -63.4 °F |
Aluminum Overlap |
3M Scotch-Weld™ 2214 Hi-Temp New Formula Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp Formula is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids,.. |
|||
Shear Strength | 19.3 MPa @Temperature 24.0 °C |
2800 psi @Temperature 75.2 °F |
Aluminum Overlap |
3M Scotch-Weld™ 2214 Hi-Temp New Formula Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp Formula is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids,.. |
|||
Shear Strength | 19.3 MPa @Temperature 82.0 °C |
2800 psi @Temperature 180 °F |
Aluminum Overlap |
3M Scotch-Weld™ 2214 Hi-Temp New Formula Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp Formula is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids,.. |