- Polymer Property : Shear Strength = 2000 psi
Polymer Property : Shear Strength = 2000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Shear Strength | 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
ASTM D1002-64 |
| 3M Scotch-Weld™ 3532 B/A Brown Two-Part Urethane Adhesive 3532 B/A Brown
(discontinued **) Two-part urethane adhesives cure at room temperature or with heat to provide tough, impact resistant bonds with high peel strength. Features include fast cure adhesive, 20-30 minutes handling stren.. |
|||
| Shear Strength | 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
ASTM D1002-64 |
| 3M Scotch-Weld™ 3535 B/A Off-white Two-Part Urethane Adhesive 3535 B/A Off-white
(discontinued **) Two-part urethane adhesives cure at room temperature or with heat to provide tough, impact resistant bonds with high peel strength. Features include fast cure adhesive, 15-20 minutes handling stren.. |
|||
| Shear Strength | 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
ASTM D1002-64 |
| 3M Scotch-Weld™ 3549 B/A Brown Two-Part Urethane Adhesive 3549 B/A Brown
(discontinued **) Two-part urethane adhesives cure at room temperature or with heat to provide tough, impact resistant bonds with high peel strength. Features include long worklife adhesive, 2-4 hours handling stren.. |
|||
| Shear Strength | 13.8 MPa @Temperature 93.3 °C |
2000 psi @Temperature 200 °F |
ASTM D732 |
| Greene Tweed Avalon® 7 PTFE, Pigmented and Molybdenum Filled Products made from Avalon® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin.. |
|||
| Shear Strength | >= 13.8 MPa @Temperature 23.9 °C |
>= 2000 psi @Temperature 75.0 °F |
Tensile lap, Al to Al |
| Master Bond EP46HT Epoxy Adhesive for Structural Bonding Description: Master Bond System EP46HT is a newly formulated two component high performance heat resistant epoxy resin system with excellent mechanical strength and chemically resistant properties f.. |
|||
| Shear Strength | 13.8 MPa @Temperature 149 °C |
2000 psi @Temperature 300 °F |
Single Lap Shear (Metal/Metal), 0.05 psf, No conditioning |
| Hexcel® Redux® 330K Epoxy film adhesives for the bonding and finishing of composites Redux 330 is a 350°F curing tough film adhesive which is ideally suited to structural bonding, composite to composite bonding, surface finishing, electromagnetic shielding and lightning strike appl.. |
|||
| Shear Strength | 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
Overlap |
| 3M Scotch-Weld™ 1838 B/A Tan Two-Part Structural Adhesive Multi-purpose and Rigid bondsInformation provided by 3M |
|||
| Shear Strength | 13.8 MPa @Temperature -55.0 °C |
2000 psi @Temperature -67.0 °F |
Overlap |
| 3M Scotch-Weld™ 1838L B/A Two-Part Structural Adhesive Multi-purpose and Rigid bondsInformation provided by 3M |
|||
| Shear Strength | 13.8 MPa @Temperature -53.0 °C |
2000 psi @Temperature -63.4 °F |
Aluminum Overlap |
| 3M Scotch-Weld™ 2214 Hi-Temp Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids, 3M™ Sc.. |
|||
| Shear Strength | 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
Aluminum Overlap |
| 3M Scotch-Weld™ 2214 Hi-Temp Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids, 3M™ Sc.. |
|||
| Shear Strength | 13.8 MPa @Temperature 149 °C |
2000 psi @Temperature 300 °F |
Aluminum Overlap |
| 3M Scotch-Weld™ 2214 Hi-Temp New Formula Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp Formula is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids,.. |
|||
| Shear Strength | 13.8 MPa @Temperature -40.0 °C |
2000 psi @Temperature -40.0 °F |
Overlap, Abraded and Solvent Wiped Steel |
| 3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
| Shear Strength | 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
Overlap |
| 3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
| Shear Strength | 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
Overlap, Etched Aluminum |
| 3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
| Shear Strength | 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
Overlap, Abraded and Solvent Wiped Al |
| 3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
| Shear Strength | 13.8 MPa @Temperature -40.0 °C |
2000 psi @Temperature -40.0 °F |
Overlap, Abraded and Solvent Wiped Al |
| 3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
| Shear Strength | 13.8 MPa @Temperature -40.0 °C |
2000 psi @Temperature -40.0 °F |
Overlap, Abraded and Solvent Wiped Steel |
| 3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
| Shear Strength | 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
Overlap |
| 3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
| Shear Strength | 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
Overlap, Etched Aluminum |
| 3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
| Shear Strength | 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
Overlap, Abraded and Solvent Wiped Al |
| 3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
| Shear Strength | 13.8 MPa @Temperature -40.0 °C |
2000 psi @Temperature -40.0 °F |
Overlap, Abraded and Solvent Wiped Al |
| 3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
| Shear Strength | 13.8 MPa @Temperature -40.0 °C |
2000 psi @Temperature -40.0 °F |
Overlap, Abraded and Solvent Wiped Steel |
| 3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
| Shear Strength | 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
Overlap |
| 3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
| Shear Strength | 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
Overlap, Etched Aluminum |
| 3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
| Shear Strength | 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
Overlap, Abraded and Solvent Wiped Al |
| 3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
| Shear Strength | 13.8 MPa @Temperature -40.0 °C |
2000 psi @Temperature -40.0 °F |
Overlap, Abraded and Solvent Wiped Al |
| 3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||