Polymer Property : Shear Strength = 34.5 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	34.5 MPa @Temperature 21.1 °C	5000 psi @Temperature 70.0 °F	2 hrs @ 250°F, Metal Clamp Pressure, 6061 T6 FPL Etched
Zyvex Performance Materials Aroply™ 250 Nano-Engineered Composite Film Adhesive Aroply™ 250 Film Adhesive is a versatile, heat curing carbon-nanotube modified epoxy structural film adhesive available in a variety of film weights on a supported knitted nylon carrier. Cured adhe..
Shear Strength	34.5 MPa @Temperature 21.1 °C	5000 psi @Temperature 70.0 °F	Lap Shear, Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463.
Hexcel® Redux® 382H (0.06 psf) Film Adhesive Redux 382H is a 250°F curing modified epoxy film adhesive available in both supported and unsupported versions. Redux 382H is a versatile adhesive system suitable for bonding a wide variety of subs..
Shear Strength	34.5 MPa @Temperature 24.0 °C	5000 psi @Temperature 75.2 °F	Overlap
3M Scotch-Weld™ 2086 One-Part Epoxy Adhesives and Metal Primer High Temperature strength and High ViscosityInformation provided by 3M
Shear Strength	34.5 MPa @Temperature 82.0 °C	5000 psi @Temperature 180 °F	Overlap
3M Scotch-Weld™ 2086 One-Part Epoxy Adhesives and Metal Primer High Temperature strength and High ViscosityInformation provided by 3M
Shear Strength	34.5 MPa @Temperature 24.0 °C	5000 psi @Temperature 75.2 °F	with Scotch-Weld EW-5000; ASTM D1002-10
3M Scotch-Weld™ EC-2815 B/A FR Epoxy Adhesive 3M Scotch-Weld Epoxy Adhesive EC-2815 B/A FR is a two-component epoxy adhesive with cure at room temperature or with additional heat to form a tough, impact-resistant bond. It has excellent adhesion..
Shear Strength	34.5 MPa @Temperature 24.0 °C	5000 psi @Temperature 75.2 °F	No Primer; ASTM D1002-10
3M Scotch-Weld™ EC-2815 B/A FR Epoxy Adhesive 3M Scotch-Weld Epoxy Adhesive EC-2815 B/A FR is a two-component epoxy adhesive with cure at room temperature or with additional heat to form a tough, impact-resistant bond. It has excellent adhesion..