- Polymer Property : Vicat Softening Point = 298 °F
Polymer Property : Vicat Softening Point = 298 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 148 °C | 298 °F | Rate B/50; ASTM D1525 |
| SABIC Innovative Plastics Lexan® BFL2015 PC Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only |
|||
| Vicat Softening Point | 148 °C | 298 °F | Rate B/120; ISO 306 |
| SABIC Innovative Plastics Lexan® LUX2619 PC (Europe-Africa-Middle East) Lexan* LUX2619 Polycarbonate resin is an extrusion grade. It is UL94 V-2 rated at 1.5 mm. It was designed for high light reflectance. |
|||
| Vicat Softening Point | 148 °C | 298 °F | Rate B/120; ISO 306 |
| SABIC Innovative Plastics Lexan® 955A PC (Europe-Africa-Middle East) Lexan* 955A Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating. Lexan 955A is available in transparen.. |
|||
| Vicat Softening Point | 148 °C @Load 5.10 kg |
298 °F @Load 11.2 lb |
50°C/hr; ASTM D1525 |
| LG Chemical Lupoy 1200-15 Polycarbonate Resin Description: LUPOY PC 1200-15 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
| Vicat Softening Point | 148 °C @Load 5.10 kg |
298 °F @Load 11.2 lb |
50°C/hr; ASTM D1525 |
| LG Chemical Lupoy 1300-15 Polycarbonate Resin Description: LUPOY PC 1300-15 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
| Vicat Softening Point | 148 °C @Load 5.10 kg |
298 °F @Load 11.2 lb |
50°C/hr; ASTM D1525 |
| LG Chemical Lupoy 3010-15 Polycarbonate Resin Description: LUPOY PC 3010-15 resin is designed for injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Character.. |
|||
| Vicat Softening Point | 148 °C @Load 5.10 kg |
298 °F @Load 11.2 lb |
50°C/hr; ASTM D1525 |
| LG Chemical Lupoy 3030-15 Polycarbonate Resin Description: LUPOY PC 3030-15 resin is designed for injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Character.. |
|||
| Vicat Softening Point | 148 °C | 298 °F | 50°C/h 50N; ISO 306 |
| Mitsubishi Xantar® 22 SR FD Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Vicat Softening Point | 148 °C | 298 °F | 50°C/h 50N; ISO 306 |
| Mitsubishi Xantar® F 23 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Vicat Softening Point | 148 °C | 298 °F | 50°C/h 50N; ISO 306 |
| Mitsubishi Xantar® FC 22 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Vicat Softening Point | 148 °C | 298 °F | B/50; ISO R306 |
| Samsung Cheil Industries Infino® LS-3302A PC, Glass Filled High Impact Information provided by Samsung Cheil Industries. |
|||
| Vicat Softening Point | 148 °C | 298 °F | 50°C/hr, 50N; ISO 306 |
| Teijin Panlite® LN-2250Y Flame Resistant, Translucent Polycarbonate Resin Flame retardant and mold release grade with normal fluidity, while maintaining intrinsic transparency of polycarbonate resin. It is suitable for injection molding applications.Applications:Electric,.. |
|||
| Vicat Softening Point | 148 °C | 298 °F | 50°C/hr, 50N Load; ASTM D1525 |
| Styron CALIBREâ„¢ 301-15 Polycarbonate Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010. |
|||
| Vicat Softening Point | 148 °C | 298 °F | Rate B/50; ASTM D1525 |
| SABIC Innovative Plastics NORYL NH7112 PPE+HIPS (Asia Pacific) Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to.. |
|||
| Vicat Softening Point | 148 °C | 298 °F | Rate B/50; ISO 306 |
| SABIC Innovative Plastics NORYL NH7112 PPE+HIPS (Asia Pacific) Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to.. |
|||
| Vicat Softening Point | 148 °C | 298 °F | Rate B/50; ASTM D 1525 |
| SABIC Innovative Plastics Xenoy® X3108UV PBT+PC (Asia Pacific) Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was sup.. |
|||
| Vicat Softening Point | 148 °C | 298 °F | 50°C/hr, 50N Load; ASTM D1525 |
| Styron CALIBREâ„¢ 201-15 Polycarbonate Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010. |
|||
| Vicat Softening Point | 148 °C @Load 5.10 kg |
298 °F @Load 11.2 lb |
Rate A (50°C/h); ASTM D1525 |
| Styron CALIBREâ„¢ 303V-6 Polycarbonate Resin Overview: CALIBREâ„¢ 303V-6 Polycarbonate resins offer exceptional impact resistance and heat distortion resistance, and meets UL94 V-2 rating. CALIBRE 303V-6 contains a mold release agent, a UV .. |
|||
| Vicat Softening Point | 148 °C | 298 °F | B/50; ISO R306 |
| Samsung Cheil Industries Infino® LF-1025 PC, Unreinforced Anti-Abrasion Information provided by Samsung Cheil Industries. |
|||
| Vicat Softening Point | 148 °C | 298 °F | B/120; ISO R306 |
| Samsung Cheil Industries Infino® SI-3109GL PC, Glass Filled High Impact Information provided by Samsung Cheil Industries. |
|||
| Vicat Softening Point | 148 °C | 298 °F | 10N-50°C per hour; ISO 306 |
| Total PPH 9081 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 9081 is a controlled-rheology homopolymer. PPH 9081 is characterized by a narrow molecular weight distribution and excellent flow properties, providing improved impact res.. |
|||
| Vicat Softening Point | 148 °C | 298 °F | ASTM D1525 |
| Total PPC 4824WZ Polypropylene, Impact Copolymer ATOFINA 4824WZ is a nucleated impact copolymer. 4824WZ is characterized by improved stiffness and impact resistance, as well as low shrinkage and low warpage. It has been formulated for excellent .. |
|||
| Vicat Softening Point | 148 °C | 298 °F | |
| Covestro Makrolon® 3208 Polycarbonate Injection molding and extrusion grade with high viscosity, BgVV- and FDA grade for food contact applications, yields especially tough parts, better resistance to hot water.Information provided by Ba.. |
|||
| Vicat Softening Point | 148 °C | 298 °F | 50°C/h 50N; ISO 306 |
| Covestro Makrolon® LTG3123 Polycarbonate PreprocessingMax. Water content |
|||
| Vicat Softening Point | 148 °C | 298 °F | |
| Covestro Makrolon® KU 1-1242 Polycarbonate, High Impact High viscosity, impact modified grade with good toughness at low temperatures (light colors only).Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer.. |
|||
| Vicat Softening Point | 148 °C | 298 °F | ISO 306/A50 |
| Addiplast Addilene PMD 50218 Flame Retardant Polypropylene Flame retardant, unreinforced, with halogensInformation provided by Addiplast. |
|||
| Vicat Softening Point | 148 °C | 298 °F | Loading 1 (10N); ASTM D1525 |
| Teknor Apex Sinpolene CPP1020 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Calcium Carbonate Filler, 20% Filler by Weight Features: Homopolymer Uses: Appliance Components; Furniture; Housings F.. |
|||
| Vicat Softening Point | 148 °C | 298 °F | Rate B/50; ASTM D 1525 |
| SABIC Innovative Plastics Lexan® ML6230 PC Copolymer (Asia Pacific) Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. Available in transparent and tinted colors.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Vicat Softening Point | 148 °C | 298 °F | 50°C/h 50N; ISO 306 |
| Mitsubishi Xantar® F 22 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances wher.. |
|||
| Vicat Softening Point | 148 °C | 298 °F | ISO 306/A50 |
| ExxonMobil PP7064L1 Polypropylene Impact Copolymer Product Description: A nucleated impact copolymer resin with medium flow, high stiffness and antistatic properties. It is suitable for molding applications like consumer products, closures, contain.. |
|||