Polymer Property : CTE, linear, Transverse to Flow = 84.0 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 20.0 °C |
46.7 µin/in-°F @Temperature 68.0 °F |
ISO data |
| BASF Capron® HPN 9333G Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9333G is a 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface a.. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 20.0 °C |
46.7 µin/in-°F @Temperature 68.0 °F |
ISO data |
| BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9333G HS is a heat stabilized, 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with.. |
|||
| CTE, linear, Transverse to Flow | 84.0 - 120 µm/m-°C | 46.7 - 66.7 µin/in-°F | Average value: 103 µm/m-°C Grade Count:14 |
| Overview of materials for Polybutylene Terephthalate (PBT), Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Flame Retardant". Each property range of values reported is minimum an.. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP LUBRICOMP 5CL23 FP-V (PVDF) LNP* LUBRICOMP* 5CL23 is a compound based on PVDF resin containing 15% Carbon Fiber, 10% PTFE. Added features include: Wear Resistant. |
|||
| CTE, linear, Transverse to Flow | 84.0 - 110 µm/m-°C @Temperature 23.0 °C |
46.7 - 61.1 µin/in-°F @Temperature 73.4 °F |
|
| Manifattura Cattaneo RULON® W2 Polytetrafluoroethylene Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP LUBRICOMP MX06404 PP LNP LUBRICOMP* MX06404 is a compound based on Polypropylene resin containing 20% Glass Fiber and 15% PTFE. Added features of this material include: Heat Stabilized, Low Extractable, Wear Resistant... |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP LUBRICOMP RFL46ES PA 66 LNP* LUBRICOMP* RFL46ES is a compound based on Nylon 6/6 containing 30% Glass Fiber, 20% PTFE. Added features of this grade include: Wear Resistant, Heat Stabilized, Easy Molding. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP LUBRICOMP WAL34 PBT LNP* LUBRICOMP* WAL34 is a compound based on (PBT resin containing 15% PTFE, 20% Aramid Fiber. Added features of this material include: Wesr Resistant. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
46.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP LUBRILOY UX99725 PPA LNP LUBRILOY* UX99725 is a compound based on Polyphthalamide resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP THERMOCOMP MX95318 PP LNP* THERMOCOMP* MX95318 is a compound based on Polypropylene containing Proprietary Filler(s). |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP THERMOCOMP RF004XXH PA 66 LNP THERMOCOMP* RF004XXH is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| SABIC Innovative Plastics LNP Thermocomp RF006PS PA 66 LNP* Thermocomp* RF-1006 EP HS is based on Nylon 6/6 containing Glass Fiber. Characteristics of this grade include Exceptional Processing and Heat Stabilizer.This data was supplied by SABIC-IP for .. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
46.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP Thermocomp RF00ASXP PA6.6 (Europe-Africa-Middle East) LNP* THERMOCOMP* RF00ASXP is a compound based on PA 66 resin containing Glass Fiber. Added features include: Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regi.. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
46.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP THERMOCOMP RF00ASXS PA6.6 (Europe-Africa-Middle East) LNP* Thermocomp* RF00ASXS is a compound based on PA 66 resin containing Glass Fiber. Added features include: Heat Stabilized. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP THERMOCOMP RFB53XXZ PA 66 LNP* THERMOCOMP* RFB53XXZ is a compound based on Nylon 66 resin containing 15% Glass Fiber, 25% Glass Bead. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP THERMOCOMP RX00713H PA 66 LNP* Thermocomp* RX00713H is a compound based on Nylon 6/6 containing proprietary fillers. Characteristics of this grade are: Healthcare. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 23.0 - 200 °C |
46.7 µin/in-°F @Temperature 73.4 - 392 °F |
ASTM D696 |
| Dalau Dalcon 006 75% Virgin PTFE, 25% Glass Fiber Applications & Industries:General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperatures.. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 23.0 - 200 °C |
46.7 µin/in-°F @Temperature 73.4 - 392 °F |
ASTM D696 |
| Dalau Dalcon 025 75% Virgin PTFE, 25% Glass Fiber, Blue Applications & Industries: General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperature.. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 23.0 - 200 °C |
46.7 µin/in-°F @Temperature 73.4 - 392 °F |
ASTM D696 |
| Dalau Dalcon 006 75% Virgin PTFE, 25% Glass Fiber Applications & Industries:General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperatures.. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 23.0 - 200 °C |
46.7 µin/in-°F @Temperature 73.4 - 392 °F |
ASTM D696 |
| Dalau Dalcon 025 75% Virgin PTFE, 25% Glass Fiber, Blue Applications & Industries: General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperature.. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 55.0 - 160 °C |
46.7 µin/in-°F @Temperature 131 - 320 °F |
ISO 11359-1/-2 |
| DuPont Performance Polymers Rynite® 940 BK505 Polyethylene Terephthalate (PET)
(Unverified Data**) 40% Glass/Mineral Reinforced Polyethylene Terephthalate Rynite 940 BK505 is a 40% mica/glass reinforced modified polyethylene terephthalate with greater strength stiffness and low warpage.Informatio.. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
46.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Eurostar Staramide RF00ASXP PA66, 50% Glass Filled, Injection Molded Staramide RF00ASXP is a 50% Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as Staramide 66 G 50V S3)Information provided by Eurostar. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
46.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Eurostar Staramide RF00ASXS PA66, 50% Glass Filled, Injection Molded Staramide RF00ASXA is a 50% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C | 46.7 µin/in-°F | ISO 11359 |
| BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Dry) Ultramid 8333G HI is a 14% glass reinforced, impact modified PA6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a
balance of st.. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 20.0 °C |
46.7 µin/in-°F @Temperature 68.0 °F |
ISO data |
| BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8333G HI is a 33% glass reinforced, impact modified polyamide 6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance .. |
|||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
46.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP LUBRICOMP CL002 PS (Europe-Africa-Middle East) LNP* LUBRICOMP* CL002 is a compound based on Polystyrene resin containing PTFE. Added features include: Internally Lubricated. |
|||