Polymer Property : CTE, linear = 11.3 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.3 µm/m-°C @Temperature 20.0 - 100 °C |
6.30 µin/in-°F @Temperature 68.0 - 212 °F |
|
| International Mold Steel NAK55 Precipitation Hardened Mold Steel Description: NAK55 is a precipitation, or age-hardened mold steel with a through hardness of approximately 40 HRc. NAK55 is ideal for use in plastic and rubber molds and other applications where imp.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 26.7 - 204 °C |
6.30 µin/in-°F @Temperature 80.0 - 400 °F |
|
| International Mold Steel Premium H13 Hot Work Die and Mold Steel Description: International Mold Steel's Premium H-13 is a chromium-based, hot work die and plastic mold steel designed for increased production rates and longer tool life. It meets the restricti.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 25.0 - 200 °C |
6.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 21.0 - 204 °C |
6.28 µin/in-°F @Temperature 69.8 - 399 °F |
|
| Latrobe LSSâ„¢ H13 PQ Hot Work Tool Steel TLS H13 PQ is Premium Quality H13 hot work steel that is designed to meet the highest quality standards in the die casting industry, and to excel in the most demanding hot work tooling applications... |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 21.0 - 204 °C |
6.28 µin/in-°F @Temperature 69.8 - 399 °F |
|
| Latrobe LSSâ„¢ H13 Tool Steel (ASTM H13) TLS H13 tool steel is a versatile chromium-molybdenum hot work steel that is widely used in hot work and cold work tooling applications. The hot hardness (hot strength) of H13 resists thermal fatigu.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 20.0 - 100 °C |
6.28 µin/in-°F @Temperature 68.0 - 212 °F |
|
| International Mold Steel DHA-World Die Cast & Forging Steel DHA-World is a high hardenability and high tough general use hot work die steel.Information provided by International Mold Steel |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 25.0 - 200 °C |
6.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 25.0 - 200 °C |
6.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 25.0 - 200 °C |
6.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 25.0 - 200 °C |
6.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 25.0 - 200 °C |
6.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 25.0 - 200 °C |
6.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 242® alloy, cold rolled sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 18.0 - 93.0 °C |
6.28 µin/in-°F @Temperature 64.4 - 199 °F |
|
| Latrobe Lescalloy® 4340 VAC-ARC ; 10.5" square High Strength Alloy Steel LESCALLOY 4340 VAC-ARC steel is a low alloy, nickel-chromium-molybdenum steel capable of being heat treated to high strength levels. The alloy has a good combination of ductility, toughness and str.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 21.0 - 204 °C |
6.28 µin/in-°F @Temperature 69.8 - 399 °F |
|
| Latrobe Viscount 44® Prehardened Tool Steel (ASTM H13S) Viscount 44 is a free-machining, prehardened, H13-type hot work tool steel. It is produced using special melting, forging, and heat treating processes which provide the optimum in control
and reprod.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 21.1 - 93.3 °C |
6.30 µin/in-°F @Temperature 70.0 - 200 °F |
H1075 |
| Crucible Steel 15-5 Precipitation Hardening Stainless Steel Crucible 15-5 is a Premium Quality precipitation-hardening stainless steel which is capable of high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is a V.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 21.1 - 427 °C |
6.30 µin/in-°F @Temperature 70.0 - 800 °F |
A |
| Crucible Steel 17Cr-4Ni Precipitation Hardening Stainless Steel Crucible 17Cr-4Ni is a precipitation-hardening stainless steel which is capable of a high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is martensitic a.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 21.1 - 93.3 °C |
6.30 µin/in-°F @Temperature 70.0 - 200 °F |
H1075 |
| Crucible Steel 17Cr-4Ni Super-X® Precipitation Hardening Stainless Steel Crucible 17Cr-4Ni is a version of 17CR-4Ni which has been modified to substantially improve machinability and other properties. Patented 17Cr-4Ni Super-X meets industry specifications for 17Cr-4Ni. .. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 21.1 - 427 °C |
6.30 µin/in-°F @Temperature 70.0 - 800 °F |
A |
| Crucible Steel 17Cr-4Ni Super-X® Precipitation Hardening Stainless Steel Crucible 17Cr-4Ni is a version of 17CR-4Ni which has been modified to substantially improve machinability and other properties. Patented 17Cr-4Ni Super-X meets industry specifications for 17Cr-4Ni. .. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 20.0 - 205 °C |
6.28 µin/in-°F @Temperature 68.0 - 401 °F |
|
| Crucible Steel AIRDI® 150 (AISI D2) Tool Steel Airdi 150 (AISI D2) is an air-hardening, high carbon, high chromium tool steel, heat treatable to HRC 60-62. It offers excellent abrasion resistance, due to a large volume of carbides in the microst.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 21.1 - 93.3 °C |
6.30 µin/in-°F @Temperature 70.0 - 200 °F |
|
| Crucible Steel WR-95 Tool Steel, AISI H10 Modified WR-95 is a modified H10, with cobalt added to improve its high temperature properties. It is an upgrade from H13 in applications requiring improved hot hardness or heat check resistance, at a slight.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 500 °C |
6.28 µin/in-°F @Temperature 932 °F |
|
| Bohler-Uddeholm BÖHLER S390 MICROCLEAN® High Speed Steel Description: High speed steel produced by powder-metallurgy methods with highest red hardness, compressive strength and wear resistance. The PM technology imparts to the material also excellent toug.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.28 µin/in-°F @Temperature 69.8 - 199 °F |
|
| AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1075 AK Steel 15-5 PH® provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, .. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature <=427 °C |
6.28 µin/in-°F @Temperature <=801 °F |
|
| AK Steel 17-4 PH® Precipitation Hardening Stainless Steel, Condition A AK Steel 17-4 PH® provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.28 µin/in-°F @Temperature 69.8 - 199 °F |
|
| AK Steel 17-4 PH® Precipitation Hardening Stainless Steel, Condition H 1075 AK Steel 17-4 PH® provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature -17.8 - 281 °C |
6.30 µin/in-°F @Temperature 0.000 - 538 °F |
|
| AK Steel 430 ULTRA FORM® Stainless Steel 430 ULTRA FORM® Stainless Steel was developed as a more formable version of Type 430 stainless steel. It is particularly suited for parts requiring more complex shapes. 430 ULTRA FORM Stainless Ste.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 20.0 - 100 °C |
6.28 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Carpenter R.D.S.® Alloy Tool Steel (Oil-Hard) (AISI L6) R.D.S. tool steel is an oil hardening die steel which combines extreme toughness with very little size change when heat treated. It is available as a DeCarb-Free product. DCF bars have been cold fin.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 20.0 - 800 °C |
6.28 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| ATI Allegheny Ludlum Type 441 Alloy Stainless Steel Allegheny Ludlum stainless Type 441 alloy is a heat resisting ferritic grades providing good oxidation and corrosion resistance for applications like automotive exhaust system components. Dual stab.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 20.0 - 800 °C |
6.28 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| ATI Allegheny Ludlum Type AL 441HP™ Stainless Steel Alloy Allegheny Ludlum stainless Type AL 441HP™ alloy is a heat resisting ferritic grade providing good oxidation and corrosion resistance for applications like automotive exhaust system components. Dua.. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 21.1 - 302 °C |
6.30 µin/in-°F @Temperature 70.0 - 575 °F |
|
| Schmolz + Bickenbach Cryodur® 2510 (O-1) Cold Work Die Steel Description: Cyrodur ® 2510 is a single melt Extra Fine Structure (EFS) material; and Supplied in the soft annealed conditionCharacteristics: Excellent dimensional stability during heat treatment; .. |
|||
| CTE, linear | 11.3 µm/m-°C @Temperature 20.0 - 200 °C |
6.28 µin/in-°F @Temperature 68.0 - 392 °F |
|
| ATI Allegheny Ludlum ALFA-II™ Stainless Steel Type 406 Characteristics:superior oxidation resistance for the temperature range 1600°F-over 2200°F, high electrical resistivity, high resistance to sulfidation, high resistance to carburization. Applicat.. |
|||