Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 600 °C |
7.17 µin/in-°F @Temperature 68.0 - 1110 °F |
|
Kennametal Stellite Nucalloy® 453 High-Silicon Nickel-Base Hardfacing Alloy Applications include chemical control valves, nuclear globe valves, nuclear gate valves, nuclear sliding parts, and pressure bars for plywood cutters.Nucalloy® alloys are unique, patented, high-s.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 0.000 - 400 °C |
7.17 µin/in-°F @Temperature 32.0 - 752 °F |
|
Kennametal Stellite Stellite® 3 PM cast Typical applications include (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) diesel engine exhaust, fluid valve seats, saw cutt.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 0.000 - 300 °C |
7.17 µin/in-°F @Temperature 32.0 - 572 °F |
|
Kennametal Stellite Stellite® 12 Satisfactory finishing results can be obtained using carbide tipped tools. Applications include cutting plastics, rubber, paper, carpet, and wood; saw teeth, trimmer knives, carpet knives, ledger bl.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 400 °C |
7.17 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 400 °C |
7.17 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 100 °C |
7.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
HP Alloys Alloy 718, 30% Cold Worked, Aged 30% Cold Worked, Aged applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Int.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 100 °C |
7.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
HP Alloys Alloy 718, 50% Cold Worked 50% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 500 °C |
7.17 µin/in-°F @Temperature 68.0 - 932 °F |
|
Bohler-Uddeholm BÖHLER W400 VMR® H11 Hot Work Tool Steel W400 VMR is a low silicon, chromium-vanadium hot work tool steel which has been vacuum remelted to obtain the highest uniformity, the best cleanliness of tool steel. The material is characterized:E.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 500 °C |
7.17 µin/in-°F @Temperature 68.0 - 932 °F |
|
Bohler-Uddeholm BÖHLER W403 VMR® Hot Work Tool Steel W403 VMR is a modified hot work alloy with an excellent combination of hot tensile properties and toughness. The balanced properties of this grade are not only due to chemistry modification, but to .. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 100 °C |
7.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
HP Alloys Alloy 718, 30% Cold Worked 30% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 100 °C |
7.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
HP Alloys Alloy 718, 5% Cold Worked 5% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internatio.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 100 °C |
7.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
HP Alloys Alloy 718, 5% Cold Worked, Aged 5% Cold Worked, Aged applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Inte.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 100 °C |
7.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
HP Alloys Alloy 718, 50% Cold Worked, Aged 50% Cold Worked, Aged applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Int.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 400 °C |
7.17 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
CTE, linear | 12.9 µm/m-°C @Temperature 21.0 - 93.0 °C |
7.17 µin/in-°F @Temperature 69.8 - 199 °F |
|
Latrobe LSS™ P20 Mold Steel (ASTM P20) TLS P20 mold steel is a versatile, low-alloy tool steel that is characterized by good toughness at moderate strength levels. The steel is commonly used for plastic injection mold cavities and toolin.. |