- Polymer Property : CTE, linear = 7.44 µin/in-°F
Polymer Property : CTE, linear = 7.44 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.4 µm/m-°C @Temperature 0.000 - 400 °C |
7.44 µin/in-°F @Temperature 32.0 - 752 °F |
|
| Kennametal Stellite Stellite® 12 PM with P/M Processing Applications: include vane plugs, fuel metering pins, spacer bushings, ball blanks (bearings), race blanks (bearings), diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wea.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 538 °C |
7.44 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 538 °C |
7.44 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Haynes Hastelloy® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 400 °C |
7.44 µin/in-°F @Temperature 69.8 - 752 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 24.0 - 538 °C |
7.44 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| HP Alloys Alloy C-276, 20% Cold Worked 20% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 300 °C |
7.44 µin/in-°F @Temperature 69.8 - 572 °F |
Mean |
| Special Metals INCONEL® 725 Nickel Superalloy (UNS N07725), Age Hardened Tube Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Age Hardened Tube samples. Other property values are typical of INCONEL® alloy 725.Data provi.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 300 °C |
7.44 µin/in-°F @Temperature 69.8 - 572 °F |
Mean |
| Special Metals INCONEL® 725 Nickel Superalloy (UNS N07725), Annealed Round Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Annealed Round samples. Other property values are typical of INCONEL® alloy 725.Data provided.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 300 °C |
7.44 µin/in-°F @Temperature 69.8 - 572 °F |
Mean |
| Special Metals INCONEL® 725 Nickel Superalloy (UNS N07725), Annealed Tube Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Annealed Tube samples. Other property values are typical of INCONEL® alloy 725.Data provided .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature -75.0 °C |
7.44 µin/in-°F @Temperature -103 °F |
|
| CRP Technology AMC225xe Aluminum Alloy - SiC Composite, T4 Condition AMC225xe is a high quality aerospace grade aluminum alloy (AA2124) reinforced with 25% by volume of ultrafine particles of silicon carbide. It is manufactured by a special powder metallurgy route us.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 732°C/8hr/FC to 621°C/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Cold Drawn 37.5% Plus Aging 649°C (1200°F)/4hr/FC to 579°C/4hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 718°C (1325°F)/8hr/AC to 621°C (1150°F)/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 538 °C |
7.44 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 538 °C |
7.44 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 24.0 - 538 °C |
7.44 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| HP Alloys Alloy C-276, 30% Cold Worked 30% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||