Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
Network Polymers NPP 30-0200 TF20 Description: 20% Talc Filled Homopolymer PolypropyleneInformation provided by Network Polymers Inc. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYfill PP CIP15015 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYfill PP CIP6015F Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycoloy® MC8002 PC+ABS AUTOMOTIVE. Low viscosity, high impact and ductility. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer 18 MFR LEXAN High Flow Ductile Copolymer UV-stabilized, available in transparent colors only |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer (Asia Pacific) 18 MFR LEXAN High Flow Ductile Copolymer UV-stabilized, available in transparent colors only |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Lexan® HFD1262 PC Copolymer (Asia Pacific) 19 MFR LEXAN High Flow Ductile Copolymerwith 400 nm cut off, available in transparent colors only |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Lexan® HFD1262 PC Copolymer (Europe-Africa-Middle East) 19 MFR LEXAN High Flow Ductile Copolymer with 400 nm cut off, available in transparent colors only |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
RheTech Products HP506-01A 21% Talc Reinforced High Performance Polypropylene, UV Stabilized, Black Applications: Automotive interior applicationsHVAC ductsTail lamp housingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYfill PP CIP6015F VTUV Polypropylene, Mineral Reinforced, Heat and UV Stabilized Information provided by Polykemi AB |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycoloy® C1110 PC+ABS High impact and ductility at 73F (23C) and -20F (-29C). |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycoloy® C1110 PC+ABS (Asia Pacific) High impact and ductility at 73F (23C) and -20F (-29C). |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics Lexan® EXRL0682 PC Copolymer 18 MFR LEXAN High Flow Ductile CopolymerThis data was supplied by SABIC-IP for the Americas region. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
ASTM D648 |
Kingfa JH950-502 Low-temperature Resistant & Flame Retardant PC/ABS Alloy Features:UL V-0 @ 3.2mmExcellent balance propertiesGood low temperature resistanceGood normal/low temperature impact strengthGood surfaceApplications:ControllerPlugSocketShell of ammeterInformation .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 B |
Metabolix Mirel™ F1006 Injection Molding Grade PHA Bioplastic Mirel F1006 is FDA cleared for use in non-alcoholic food contact applications, from frozen food storage and microwave reheating to boiling water up to 212°F. FDA clearance includes products such.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ISO 75-1,-2 |
Inno-Comp INNOPOL® CS 1-3260 55% Chalk-Filled Polypropylene Homopolymer INNOPOL® CS 1-3260 is a 55% chalk-filled polypropylene homopolymer compound /PP-H KD55 (ISO 1043)/. This grade is available in natural and custom colored form.INNOPOL® CS 1-3260 is developed f.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ISO 75-1,-2 |
Inno-Comp INNOPOL® CS 2-3120 20% Talc Filled Polypropylene Block-Copolymer INNOPOL® CS 2-3120 is a 20% talc filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-3120 is developed for producing.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | Unannealed; ASTM D648 |
LyondellBasell Pro-faxâ„¢ SC973 Polypropylene Copolymer Description: Pro-faxâ„¢ Ultra SC973 fully formulated (antistatic, nucleated, slip modified), very high melt flow, impact polypropylene reactor copolymer resin is designed for injection molding ap.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP Lubricomp ZP003 PPE+PS (Europe-Africa-Middle East) LNP* LUBRICOMP* ZP003 is a compound based on PPE + PS Blend resin containing PTFE, Silicone. Added features include Internally Lubricated.This data was supplied by SABIC-IP for the Europe-Africa-Mid.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Xenoy® X5500EX PBT+PC (Asia Pacific) Non-FR, non-UV PC/PBT blend for film extrusion application |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | Unannealed; ASTM D648 |
Teknor Apex Sinpolene TPP2020 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Talc Filler, 20% Filler by Weight Uses: Appliance Components; Automotive Applications; Housings Forms: Pellets Process.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ISO 75-2 |
Borealis Daplen™ EF341AE Polypropylene TPO Compound Daplen™ EF341AE is a 30% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties, gives a good surface q.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE DescriptionPolyfort® FLP 3714 is a 20% glass filled HDPE product. Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE DescriptionPolyfort® FLP 3714 is a 20% glass filled HDPE product. Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE DescriptionPolyfort® FLP 3714 is a 20% glass filled HDPE product. Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE DescriptionPolyfort® FLP 3714 is a 20% glass filled HDPE product. Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
ExxonMobil PP1222F Mineral-filled Homopolymer Medium melt flow rate homopolymer, 20% filled. Particularly suitable for consumer products and appliance applications requiring long term heat aging resistance. UL continuous service rating of 95°.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
Aclo Accutech Polypropylene Copolymer CP0436M40L Mica Reinforced |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
Braskem H 117 Injection Molding Polypropylene Description: H 117 is a ultra-high melt flow rate homopolymer. This product is suitable to high productivity on thin-walled parts. H 117 features an excellent stiffness, thermal resistance, low warp.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 254 °F | HDT/A; ASTM D648 |
GEHR Plastics Noryl PPO
(discontinued **) PPO belongs to the group of the amorphous materials and can be used in temperatures ranging from -58 °F to +302 °F. PPO exhibits a high impact strength and a very high dimensional stability. The e.. |