Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 42.0 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	42.0 °C	108 °F	ASTM D648
NOVA Chemicals Sclair® 8107 UV8D Butene LLDPE Rotational Molding Resin Excellent ESCR, Excellent low temperature impact properties, Excellent low shrinkage and warpage properties, Very good processability, UL 94-HB listedApplications: Food and laundry materials handlin..
Deflection Temperature at 0.46 MPa (66 psi)	42.0 °C	108 °F	ASTM D648
NOVA Chemicals Sclair® 8107G UV8D Butene LLDPE Rotational Molding Resin Excellent ESCR, Excellent low temperature impact properties, Excellent low shrinkage and warpage properties, Very good processability, UL 94-HB listedApplications: Food and laundry materials handlin..
Deflection Temperature at 0.46 MPa (66 psi)	42.0 Â°C	108 Â°F	ASTM D648
LyondellBasell PetrotheneÂ® NA940000 Low Density Polyethylene (Blow Molding) ApplicationsPETROTHENE NA 940-000 is a low density homopolymer resin intended for use in blow molding applications. Excellent toughness, good clarity and processability make NA 940-000 an ideal cho..
Deflection Temperature at 0.46 MPa (66 psi)	42.0 Â°C @Thickness 3.20 mm	108 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP PDXF89080 PE LNP* LUBRICOMP* PDXF89080 is a compound based on Polyethylene containing Proprietary Fillers. Added feature of this grade is: Wear Resistant.
Deflection Temperature at 0.46 MPa (66 psi)	42.0 °C	108 °F	ASTM D648
DuPont™ Surlyn® 8660 Ionomer Resin, Sodium Surlyn® 8660 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neu..
Deflection Temperature at 0.46 MPa (66 psi)	42.0 °C	108 °F	ASTM D648
DuPont™ Surlyn® 9520 Ionomer Resin, Zinc Surlyn® 9520 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr..
Deflection Temperature at 0.46 MPa (66 psi)	42.0 °C	108 °F	ASTM D648
Arkema Group Pebax® 2533 Polyether Block Amide (PEBA) Information provided by Arkema Group
Deflection Temperature at 0.46 MPa (66 psi)	42.0 °C	108 °F
Arkema Group Pebax® 2533 SN 01 Polyether Block Amide (PEBA) (Conditioned) POLYETHER BLOCK AMIDE (PEBA) hardness 25 shore D Non plasticized flexible Polyamide Outstanding mechanical properties at low temperature (-40°C) Applications: molded parts for sport goods (softness..
Deflection Temperature at 0.46 MPa (66 psi)	42.0 - 57.2 °C	108 - 135 °F	Average value: 48.9 °C Grade Count:11
Overview of materials for Linear Low Density Polyethylene (LLDPE), Injection Molded This property data is a summary of similar materials in the MatWeb database for the category "Linear Low Density Polyethylene (LLDPE), Injection Molded". Each property range of values reported is mi..
Deflection Temperature at 0.46 MPa (66 psi)	42.0 - 106 °C	108 - 223 °F	Average value: 72.4 °C Grade Count:25
Overview of materials for Polyether Block Amide (PEBA) This property data is a summary of similar materials in the MatWeb database for the category "Polyether Block Amide (PEBA)". Each property range of values reported is minimum and maximum values of a..
Deflection Temperature at 0.46 MPa (66 psi)	42.0 °C	108 °F	ASTM D648
LATI LATISTAT 48/9900-03 Ethylene Vinyl Acetate (EVA) Base Conductive Plastic (Unverified Data**) Description: Latistat materials have low specific resistivity. They feature partial electrical conductivity. Selected functional additives give materials with low specific resistivity and reasonable..