Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | ASTM D-648 |
Plaskolite Optix® CA - 51 LL General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | ASTM D-648 |
Plaskolite Optix® CA - 51 UVT General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | ASTM D-648 |
Plaskolite Optix® CP - 51 General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C @Thickness 3.18 mm |
168 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ Vinyl Rigid Extrusion 87345 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | ASTM D-648 |
Plaskolite West Optix® CA - 51 FDA General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | ASTM D-648 |
Plaskolite West Optix® CP - 51 KC General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | ASTM D-648 |
Plaskolite West Optix® CA - 51 KC General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | ASTM D-648 |
Plaskolite West Optix® CA - 51 LL General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | ASTM D-648 |
Plaskolite West Optix® CP - 51 General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | ASTM D648 |
RheTech Products HP525-01 30% Talc Reinforced High Performance Polypropylene, UV Stabilized, Black Applications: Center consolesInterior trimInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | Unannealed; ASTM Data |
Americas Styrenics Styron® 615APR Polystyrene
(discontinued **) STYRON® 615 APR is a general purpose easy flow resin typically used for medical, pharmaceutical and thin-walled parts. It is an excellent resin for blending with K-Resin (K-Resin is a trademark of .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.5 °C | 168 °F | annealed; ASTM D648 |
Kleerdex Kydex® L Acrylic/PVC Thermoplastic Sheet
(discontinued **) Laminating grade fire rated sheetApplications: Store fixtures and displays, exhibits, service counters, doors, partitionsFeatures: Toughness and durability, solid, integral color, chemical resistanc.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | ASTM D648 |
KYDEX® 152WG Capped Wood Grain Thermoplastic Sheet Features:Super tough, durableHigh extensibility, rigidity, abrasion resistance and fire retardancyMore rigid than most thermoplastics, parts deform less when loadedOutstanding resistance to breakage.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.5 °C | 168 °F | annealed; ASTM D648 |
KYDEX® 311 Co-Extruded High Impact Fire-Rated Thermoplastic Sheet Features:Color-matched cap, black or off-white substrateThickness ranging from 1.5 mm to 8.9 mmToughness and durabilityEasy to form with good part definitionChemical resistantFire retardantExcellent.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.5 °C | 168 °F | annealed; ASTM D648 |
KYDEX® 311 MB Co-Extruded High Impact Fire-Rated Thermoplastic Sheet with Microban® Antimicrobial Features:Color-matched cap, black or off-white substrateThickness ranging from 1.5 mm to 8.9 mmToughness and durabilityEasy to form with good part definitionChemical resistantFire retardantExcellent.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.5 °C | 168 °F | annealed; ASTM D648 |
KYDEX® T Acrylic/PVC Thermoplastic Sheet Impact resistant fire rated sheetApplications: External housings for equipment such as photocopy machines, instrument panels, computers, keyboards, telephones, internal parts for equipment such as v.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.5 °C | 168 °F | annealed; ASTM D648 |
KYDEX® 331/331d Co-Extruded High Impact Fire Rated Thermoplastic Sheet with Weatherable Acrylic Film Cap KYDEX® 331 is a co-extruded high impact fire rated thermoplastic sheet with a weatherable cap that offers superior performance for thermoforming. It can also be used as an impact resistant surfa.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | annealed; ASTM D648 |
KYDEX® T MB High Impact Fire Rated Thermoforming Sheet with Microban® Antimicrobial Product Features:Substitute for FR-ABS sheet with competitive pricing but superior cost/performanceHigher breakage resistanceStandard thicknesses from 0.71 mm to 2.36 mmAmong the most rigid of thermoforming.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | unannealed, .125in; ASTM D648 |
Star Plastics ABSFR1 Molding Grade ABSFR Information provided by Star Plastics, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | unannealed, .125in; ASTM D648 |
Star Plastics ABSFR2 Molding Grade ABS Information provided by Star Plastics, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | Unannealed; ASTM D648 |
Techmer ES Plastiblend® ABS/PA 1700 B2 Availability: North AmericaForms: PelletsAppearance: Natural ColorProcessing Method: ExtrusionInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.3 °C | 168 °F | ASTM D648 |
A. Schulman POLYFLAM™ RABS 930-01 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.3 °C | 168 °F | ASTM D648 |
A. Schulman POLYFLAM™ RABS 930-01 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.3 °C | 168 °F | ASTM D648 |
A. Schulman POLYFLAM™ RABS 930-01 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.3 °C | 168 °F | ASTM D648 |
A. Schulman POLYFLAM™ RABS 930-01 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.3 °C | 168 °F | ASTM D648 |
A. Schulman POLYFLAM™ RABS 930-01 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | Annealed; ASTM Data |
Dow Retain® PS-4378 Polystyrene Data provided by Dow Chemical. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | unannealed; injection molded; ASTM D648 |
Americas Styrenics STYRON™ 487 High-Impact Polystyrene Resin STYRON™ 487 is a high-impact polystyrene with an excellent balance of flow, toughness, stiffness and heat resistance. It has excellent deep draw characteristics and is appropriate for extrusion ap.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | Unannealed; ASTM D648 |
Techmer ES Plastiblend® ABS/PA 1700 Availability: North AmericaForms: PelletsAppearance: Natural ColorInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C @Thickness 3.18 mm |
168 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ Vinyl Rigid Extrusion L6180 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |