- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 221 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 221 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D-648 |
| PlastiComp Complet® LGF60 - PA6 Nylon 6, 60% Long Glass Fiber Reinforced Complet® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 6 with 60% long glass reinforcementInformation provided by PlastiComp, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D-648 |
| PlastiComp Velocity® LGF60-PA6 High Flow Nylon 6, 60% Long Glass Fiber This compound complies with European Union Directive 2002/95/EC Restriction of Hazardous Substances (RoHS).Information provided by PlastiComp, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D648 |
| Oxford Polymers 30GF 30% Glass Fiber Reinforced Polybutylene Terephthalate (PBT) 30% Glass Fiber Reinforced Polybutylene Terephthalate (PBT)Information provided by Oxford Polymers. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D648 |
| Polymer Resources PPX/NY G20 PPO/Nylon 66 Alloy , 20% Glass Reinforced Polyphenylene Oxide/Nylon 66 Alloy , 20% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informa.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D648 |
| Plenco 50030 PET, Pellet, Injection Molded, Black
(discontinued **) PLENCO 50030 is an engineering grade glass reinforced polyethylene terephthalate resin designed for good physical strength. It is UL listed and available in white, natural, and black.Information sup.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D648 |
| Plenco 50030 PET, Pellet, Injection Molded, White
(discontinued **) PLENCO 50030 is an engineering grade glass reinforced polyethylene terephthalate resin designed for good physical strength. It is UL listed and available in white, natural, and black.Information sup.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D648 |
| Plenco 51130 PET, Pellet, Injection Molded, Black
(discontinued **) PLENCO 51130 is an engineering grade UL flame rated glass reinforced recycled polyethylene terephthalate resin designed for good physical strength. It is UL listed and available in black only.Inform.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D648 |
| Plenco 51240 PET, Pellet, Injection Molded, Green
(discontinued **) PLENCO 51240 is an engineering grade glass reinforced flame retarded recycled polyethylene terephthalate resin designed for excellent dimensional stability. It is UL listed.Information supplied by P.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 - 262 °C | 430 - 504 °F | Average value: 247 °C Grade Count:15 |
| Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 30% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT or PCTA, 30% Glass Reinforced".Specific grades with glass content between 25% and 34% are included. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP RX03643H PA 66 (Asia Pacific) LNP* Lubricomp* RX03643H is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6/6 GF13 IM2 BK 13% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 13% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6/6 GF13 IM2 HS L 13% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 13% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C @Thickness 6.40 mm |
430 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM CRS5301 PEI (Asia Pacific) 30% Glass fiber filled, standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 and 5VA listing. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF13 L 13% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 13% Filler by Weight Additive: LubricantFeatures: LubricatedAppearance: BlackInformation provided by TP Comp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF13 TL10 13% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 13% Filler by Weight Additive: PTFE Lubricant (10%)Features: LubricatedAppearance: Natural ColorInformation .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF14 HS L BK 14% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 14% Filler by Weight Additive: Heat Stabilizer and LubricantFeatures: Lubricated and Heat StabilizedAppearan.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF15 TL5 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by Weight Additive: PTFE Lubricant (5%)Features: LubricatedAppearance: Natural ColorInformation p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF6 L BK 6% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 6% Filler by WeightAdditive: Lubricant Features: Lubricated Appearance: BlackInformation provided by TP Comp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF7 L 7% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 7% Filler by WeightAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 GF13 SL2 13% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 13% Filler by WeightAdditive: Heat Stabilizer and Silicone LubricantFeatures: Lubricated and Heat StabilizedInformation pr.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP JF004Z PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004Z is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: HV. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C @Thickness 3.20 mm |
430 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RF003ES PA 66 LNP* THERMOCOMP* RF003ES is a Nylon 66 base resin containing 15% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP RF004 PA 66 LNP THERMOCOMP* RF004 is a compound based on Nylon 66 resin containing 20% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP RF004XXD PA 66 LNP THERMOCOMP* RF004XXD is a compound based on Nylon 66 resin containing 20% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Rynite® 530 BK503 Polyethylene Terephthalate (PET)
(Unverified Data**) 30% Glass Reinforced Polyethylene Terephthalate Rynite 530 BK503 is a 30% glass reinforced modified polyethylene terephthalate with outstanding balance of strength stiffness and toughness excellent .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C @Thickness 3.20 mm |
430 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Eurostar Staramide RF004EU PA66/6, 20% Glass Fiber Filled, Injection Molded Staramide RF004EU is a 20% Glass Fiber Reinforced Polyamide 66/6 Injection Molding (also known as Staramide 66C 20V S4)Information provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D648 |
| Ashley Polymers Ashlene® E126 PET Polyester, 30% Glass Reinforced PET Polyester, economy grade with 30% glass reinforcement.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D648 |
| Chem Polymer Chemlon 109-18 G Nylon 66, 18% Glass Fiber Reinforced A highly toughened 18% glass fiber reinforced nylon 66 developed for applications requiring stiffness, creep resistance and impact resistance.Data provided by the manufacturer, Chem Polymer. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Rynite® 530 BK503 PET
(Unverified Data**) Rynite® 530 BK503 is a 30% glass reinforced modified polyethylene terephthalate with outstanding balance of strength, stiffness, and toughness, excellent electrical properties, surface appearance, .. |
|||