- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 262 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 262 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® EX2079X PC (Europe-Africa-Middle East) Lexan* EX2079X polycarbonate resin, MVR (300°C/1.2kg) 3 cm3/10min, high viscosity, branched, extrusion, flame retardant, halogen free per DIN VDE 0472 Part 815, mold release, UV stabilized, translu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 3.20 mm |
262 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Lexan® ML7666 PC (Asia Pacific) Non FR Impact modified PC, excellent Fatigue performance with balanced Flow and impact. Available in Opaque onlyThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP DL0029E PC (Europe-Africa-Middle East) LNP* Lubricomp* DL0029E is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Flame Retardant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 3.20 mm |
262 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® 143X PC Copolymer (Asia Pacific) Improved flow PC with excellent processability and mold release. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® EX2078X PC (Europe-Africa-Middle East) Lexan* EX2078X polycarbonate resin, MVR (300°C/1.2kg) 3 cm3/10min, high viscosity, branched, extrusion, flame retardant, halogen free per DIN VDE 0472 Part 815, mold release, UV stabilized, translu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® EXL1414 PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1414 polycarbonate (PC) siloxane copolymer resin is a medium flow opaque injection molding (IM) grade. This resin offers extreme low temperature (-40 C) ductility in combination with excel.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® EXL1414H PC Copolymer Opaque PC-Siloxan copolymer with excellent processability. Medium flow, extreme low temperature ductile. Enhanced hydrolytic stability. Only available in black color. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® FL900S PC (Europe-Africa-Middle East) Foamable Lexan* FL900S polycarbonate resin is an ideal choice for structural components where load bearing capability at elevated temperature is a key requirement. It exhibits outstanding inpact str.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 3.20 mm |
262 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD4472 PC (Asia Pacific) Lexan* HFD4472 is a 20% glass filled, medium flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4472 has enhanced mold release, impact ductili.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 3.20 mm |
262 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD4472 PC (Europe-Africa-Middle East) Lexan* HFD4472 is a 20% glass filled, medium flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4472 has enhanced mold release, impact ductili.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® HPS7 PC Low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam, and gamma sterilizable. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | Unannealed; ASTM D648 |
| M. Holland Company PC402R Polycarbonate High clarityHigh heat resistanceHigh impact resistanceGood mold releaseApplications: AppliancesContainersTable products |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 6.40 mm |
262 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa PC-S809 Modified PC Features:Good mechanical propertiesSuper high impact strengthGood weather resistanceHigh glossGood processing propertiesStress cracking propertiesApplications:OA and IT partsAutomobile accessoriesEl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | ASTM D648 |
| Mitsubishi Iupilon® E2001R 5 MFI FDA Compliant Polycarbonate With Release Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | ASTM D648 |
| Mitsubishi Iupilon® H3000R 30 MFI Polycarbonate With Release Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | ASTM D648 |
| Mitsubishi Iupilon® H3000UR 30 MFI, UV Stabilized Polycarbonate With Release Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | ASTM D648 |
| Mitsubishi Iupilon® S2000UR 9.5 MFI, UV Stabilized Polycarbonate With Release Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 3.20 mm |
262 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp DX99854 PC (Asia Pacific) LNP* LUBRICOMP* DX99854 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.This data was supplied by SABIC-I.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON DD0009P PC LNP STAT-KON* DD0009P is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Exceptional Processing, Flame Retardant... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON DD0009P PC (Asia Pacific) LNP STAT-KON* DD0009P is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | ASTM D648 |
| Shuman 980 Grey Polycarbonate Good impact strength, easy processability, good surface gloss, good heat resistance, excellent weatherability, excellent color stability, self extinguishingInformation provided by Shuman Plastics, I.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | ASTM D648 |
| Shuman FR910V0 Utility Black Polycarbonate Flame Retardant Good impact strength, easy processability, good surface gloss, good heat resistance, excellent weatherability, excellent color stability, self extinguishingInformation provided by Shuman Plastics, I.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | ISO 75 |
| Teijin Panlite® LV-2225Y Standard (mold release/ice color grade) Polycarbonate Resin Flame retardant and mold release grade, while maintaining intrinsic transparency of polycarbonate resin. It is suitable for injection molding applications, required to be slightly high fluidity.Appl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | Unannealed, 0.125 in; ASTM D648 |
| Styron CALIBREâ„¢ 201-10 Polycarbonate Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 3.20 mm |
262 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DD0009PC PC LNP STAT-KON* DD0009PC is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | Unannealed, 0.125 in; ASTM D648 |
| Styron CALIBREâ„¢ 303-10 Polycarbonate Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | annealed; ISO 75 |
| Chi Mei Wonderlite® PC-115 Polycarbonate Low Viscosity |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | 0.125";; ASTM D648 |
| Diamond Polymers PC-1514LUV UV Stabilized Polycarbonate Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | |
| Asahi Kasei Xyron® G701V Modified Polyphenylene Ether Applications: Automotive: Door Handles, Fuse Carriers, Fuse Box Covers, Interior Electrical Outlets, Interior Plugs/Switches, Interior High Precision Parts Electrical and Industrial: Pool and Spa P.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Sax Polymers SAXALEN PPH325GK20 Polypropylene Homopolymer, 20% Glass Filled SAXALEN PPH325GK20 is a 10% glass-fiber and 10% glass-beads filled Polypropylene - Homopolymer intended for injection molding. It has a increased stiffness and a optimized warpage grade.Information .. |
|||