- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 59.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 59.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Extrusion 87564 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | |
| Plastcom SLOVAMID 66/6 HI/1 PA66/6, improved strength FeaturesMix of polyamide 66/6 modified with thermoplastic reactive caoutchouc, determined for mouldings with high toughness also at minus temperatures. Eligible application for ski-shoes, helmets fo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75 |
| Solvay Engineered Polymers SEQUEL® 2380 Engineered Polyolefin
(discontinued **) Description: SEQUEL® 2380 engineered polyolefin is designed for large mold-in-color automotive interior applications that require stiffness and dimensional stability over a broad temperature range... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ASTM D648 |
| Kolon SPESIN® KP270BL General Purpose PBT Compound Resin Excellent waterproofnessApplications: ConnectorsInformation provided by API-Kolon. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 7705 PP SABIC® PPcompound 7705 is a mineral filled, impact modified polypropylene TPO. This material combines impact resistance, scratch resistance, and heat stability with interior automotive UV stabili.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 9710 PP SABIC® PPcompound 9710 is a mineral filled, impact modified polypropylene TPO. This material combines high impact resistance, scratch resistance, and heat stability with interior automotive UV st.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C @Thickness 3.20 mm |
138 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RP003 PA 66 LNP* LUBRICOMP* RP003 is a compound based on Nylon 66 resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP WL003 PBT (Europe-Africa-Middle East) LNP* Lubricomp* WL003 is a compound based on Polybutylene Terephalate resin containing PTFE. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C @Thickness 3.20 mm |
138 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON WS002I PBT LNP* STAT-KON* WS002I is a compound based on PBT resin containing 10% Stainless Steel. Added features of this material include: Electrically Conductive, High Impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-LOY M3000 PP (Europe-Africa-Middle East) LNP* Stat-loy* M3000 is a compound based on Polypropylene resin. Added features of this material include: Antistat, High Impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75-1/-2 |
| Styrolution Styrolux® 693 D SBC Description: Styrolux® 693 D is a clear styrene-butadiene copolymer (SBC) with a well balanced combination of toughness and clarity. Styrolux® 693 D is mainly used for thermoformed articles, e.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP RI001 PA 66 LNP* LUBRICOMP* RI001 is a compound based on Nylon 66 resin containing 2% Silicone. Added feature of this grade is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-LOY M3000 PP LNP STAT-LOY* M3000 is a compound based on unfilled Polypropylene resin. Added feature of this material is: Antistat. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75-1/-2 |
| Unitika A1030SR PA6, Dry Information provided by Unitika Ltd. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75 |
| A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ASTM D648 |
| Formosa Plastics Formolene® 6145O Impact Copolymer Polypropylene Impact Copolymer for Appliance Applications Formolene® 6145O is a medium impact copolymer of polypropylene characterized by its easy mold flow, physical property balance and excellent dimensional s.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75 |
| A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75 |
| A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75-1, 2 |
| Polyplastics Duranex® 700FP Polybutylene Terephthalate (PBT), Unfilled PBT for film, Extrusion, High Viscosity DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75-1, 2 |
| Polyplastics Duranex® CA7200NX Polybutylene Terephthalate (PBT), Antistatic DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | DIN 53461 |
| Polyram RamOfin PPC342M6 Polypropylene, 30% Mineral Filled 30% mineral filled, heat resistant polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | |
| Covestro Texin® 4210 Urethane Thermoplastic Elastomer Key Features:UnfilledSuitable processing methods:Injection moldingFilm extrusionProfile extrusionSheet extrusionInformation provided by Bayer Polymers.As of 1 September 2015, Bayer MaterialScience w.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ASTM D648 |
| Diamond Polymers NYLON 6615 HS Natural Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ASTM-D648 |
| Braskem H 216 HOMO Polypropylene Homopolymer H 216 is a high melt flow rate homopolymer with narrow molecular weight distribution. It is designed for fiber extrusion processing with high toughness fibers. H 216 exhibits excellent processabilit.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | |
| Arkema Group Rilsan® MB 3750 Nylon 11, Transparent Grade (Dry) Designation ISO 1874-PA11/xx,F,THL,22-020Transparent semi-crystalline PA11 grade.Used for film extrusion and injection molding (low thickness).Very good low temperature impact strength.High chemical.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | |
| BASF Procom® D 1165 Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | |
| BASF Procom® D 1195 Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75 |
| A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75-2 |
| Borealis Xmod™ MC55T1 Polypropylene Compound 10% Mineral Filled Xmod MC55t1 is a 10% mineral filled grade based on HCPP intended for injection molding. Xmod has been developed especially for the car industry, to be used in interior parts. XMod offers very good .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | DIN 53461 |
| Polyram RamOfin PPC359T4 Polypropylene, 20% Mineral Filled 20% mineral filled, heat stabilized and impact modified for polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||