- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 67.2 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 67.2 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C @Thickness 3.18 mm |
153 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Packaging JGR-154A Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C @Thickness 3.18 mm |
153 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Extrusion 87547 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C @Thickness 3.18 mm |
153 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Extrusion 87554 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C @Thickness 3.18 mm |
153 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Extrusion 87555 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C @Thickness 3.18 mm |
153 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Extrusion 87556 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C @Thickness 1.57 mm |
153 °F @Thickness 0.0618 in |
Annealed; ASTM D648 |
| PolyOne Novablend™ 5035 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | Annealed, 0.125 in bars; ASTM D648 |
| PolyOne Edgetek® PS-1000 Polybutylene Terephthalate (PBT)
(discontinued **) Description/Features:UL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | ASTM D648 |
| RheTech Products HP506-01 20% Talc Reinforced High Performance Polypropylene, Black Applications: Underhood componentsLamp housingsHVAC ductsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylon® N1000THLHF2 Nylon 6/6
(discontinued **) Available in North America Additive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Lubricated, Heat Stabilized, Impact Modifier and High FlowRoHS CompliantAuto Specifications: GM GMW16447P.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | ASTM D648 |
| Spartech Solarex® SV Copolyester Sheet Description: Copolyester SheetInformation provided by Spartech. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | ASTM Test |
| Styrolution Terblend® N NMX04 ABS/PA6 (Dry) Terblend N NMX04 is an ABS/PA6 blend specially developed for painted exterior applications, combining impact resistance with excellent processability and paintability.Information provided by STYROLU.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | ASTM D648 |
| Clariant Renol PBT1100 Black Polybutylene Terephthalate, General Purpose Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | ASTM D648 |
| Clariant Renol PBT1100S Polybutylene Terephthalate, Silicone Lubricated Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | |
| Aclo Accutech Polypropylene Homopolymer HP0334M20L Mica Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | |
| Aclo Accutech Polypropylene Homopolymer HP0334T30L Talc Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | |
| Aclo Accutech Polypropylene Homopolymer HP0336W20L Wollastonite Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | |
| BCC Products BE 290 Epoxy Laminating System BE 290 is a low viscosity, medium pot life, room temperature laminating system. BE 290 features low odor, reduced toxicity and adequate working life for constructing medium and large fabricated tool.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | ASTM D648 |
| RheTech Products HP506-01B 22% Talc Reinforced High Performance Polypropylene, UV Stabilized, Black Applications: Underhood componentsLamp housingsHVAC ductsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||