Polymer Property : Maximum Service Temperature, Inert = 212 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Inert	100 °C @Thickness 0.000 mm, Time 7.20e+7 sec	212 °F @Thickness 0.000 in, Time 20000 hour	IEC 60216; IEC/EN 60893-2 7.1
Elektro-Isola Etronax MF G Phenolic, Cotton Fabric Reinforcement, Black, Sheets Description: Exclusively for mechanical applications. Impact-resistant. Resistant to mechanical wear and noise-reducing. The graphite content causes low friction. Well suited for parts where there a..
Maximum Service Temperature, Inert	100 °C @Thickness 0.000 mm, Time 7.20e+7 sec	212 °F @Thickness 0.000 in, Time 20000 hour	IEC 60216; IEC/EN 60893-2 7.1
Elektro-Isola Etronax MF Phenolic, Cotton Fabric Reinforcement, Brown, Sheets Description: Exclusively for mechanical applications. Impact-resistant, resistant to mechanical wear, noise-reducing, low friction. Well suited for parts where there are high mechanical load and wea..
Maximum Service Temperature, Inert	100 °C @Thickness 3.00 mm, Time 7.20e+7 sec	212 °F @Thickness 0.118 in, Time 20000 hour	IEC 60695-11-10; IEC/EN 61212-2 7.1
Elektro-Isola Etronax MF Phenolic, Cotton Fabric Reinforcement, Brown, Tubes Description: Mechanical applications. Impact-resistant, noise-reducing and wear-resistant material. Well suited as a low-friction material. High wear resistance in aggressive and dust-filled environ..
Maximum Service Temperature, Inert	100 °C @Thickness 0.000 mm, Time 7.20e+7 sec	212 °F @Thickness 0.000 in, Time 20000 hour	IEC 60216; IEC/EN 60893-2 7.1
Elektro-Isola Etronax MFP G Phenolic, Cotton/synthetic Fabric Reinforcement, Black, Sheets Description: Exclusively for mechanical applications. The combination of cotton/synthetic reinforcement and a graphite-modified resin results in a material with low friction and especially high wear..
Maximum Service Temperature, Inert	100 °C @Thickness 0.000 mm, Time 7.20e+7 sec	212 °F @Thickness 0.000 in, Time 20000 hour	IEC 60216; IEC/EN 60893-2 7.1
Elektro-Isola Etronax MMF Phenolic, Cotton Fabric Reinforcement, Brown, Sheets Description: Reinforced with a finer cotton fabric than Etronax MF. Also well suited in particular for small components which are subject to mechanical load and wear. Can be machined to finer tolera..
Maximum Service Temperature, Inert	100 °C @Thickness 3.00 mm, Time 7.20e+7 sec	212 °F @Thickness 0.118 in, Time 20000 hour	IEC 60695-11-10; IEC/EN 61212-2 7.1
Elektro-Isola Etronax MMF Phenolic, Cotton Fabric Reinforcement, Brown, Tubes Description: Mechanical applications. Reinforced with finer fabric than Etronax MF. Can be used, in particular, for mechanical applications where fine tolerances and smoother surface finish are requ..
Maximum Service Temperature, Inert	100 °C @Thickness 3.00 mm, Time 7.20e+7 sec	212 °F @Thickness 0.118 in, Time 20000 hour	IEC 60695-11-10; IEC/EN 61212-2 7.1
Elektro-Isola Etronax MMMF Phenolic, Cotton Fabric Reinforcement, Brown, Tubes Description: Mechanical applications. Impact-resistant, noise-reducing, wear-resistant material. Well suited as a low-friction material. High wear resistance in aggressive and dust-filled environmen..
Maximum Service Temperature, Inert	100 °C @Thickness 0.000 mm, Time 7.20e+7 sec	212 °F @Thickness 0.000 in, Time 20000 hour	IEC 60216; IEC/EN 60893-2 7.1
Elektro-Isola Etronax MMMF Phenolic, Cotton Fabric Reinforcement, Light Brown, Sheets Description: Friction reducing material consisting of phenolic resin and a very fine cotton fabric. Exclusively for mechanical applications. Good dry-run properties but can be lubricated with oil, g..
Maximum Service Temperature, Inert	100 °C @Thickness 0.000 mm, Time 7.20e+7 sec	212 °F @Thickness 0.000 in, Time 20000 hour	IEC 60216; IEC/EN 60893-2 7.1
Elektro-Isola Etronax MMMF PTFE Phenolic, Cotton Fabric Reinforcement, Light Brown, Sheets Description: Friction reducing material consisting of phenolic resin with PTFE (Teflon®) and a very fine cotton fabric. Exclusively for mechanical applications. Very good dry run properties. Well s..
Maximum Service Temperature, Inert	100 °C @Thickness 3.00 mm, Time 7.20e+7 sec	212 °F @Thickness 0.118 in, Time 20000 hour	IEC 60695-11-10; IEC/EN 61212-2 7.1
Elektro-Isola Etronax MF G Phenolic, Cotton Fabric Reinforcement, Black, Tubes Description: Mechanical applications. Impact-resistant, noise-reducing, wear-resistant material. Well suited as a low-friction material. High wear resistance in aggressive and dust-filled environmen..
Maximum Service Temperature, Inert	100 °C @Thickness 3.00 mm, Time 7.20e+7 sec	212 °F @Thickness 0.118 in, Time 20000 hour	IEC 60695-11-10; IEC/EN 61212-2 7.1
Elektro-Isola Etronax MFP G Phenolic, Cotton Fabric Reinforcement, Black, Tubes Description: Exclusively for mechanical applications. The combination of cotton/synthetic reinforcement and a graphite-modified resin results in a material with low friction and especially high wear..