3M Dyneon™ PVDF 6010/0000 Polyvinylidene Fluoride

Category Polymer , Thermoplastic , Fluoropolymer , PVDF
Manufacturer 3M Dyneon™
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ PVDF 6010/0000 Polyvinylidene Fluoride.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyvinylidene Fluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical processing industry, wire and cable industry, semiconductor industry, and oil and gas industry, PVDF is also gaining recognition in automotive, building, electronics, pharmaceutical and battery applications. 3M™ Dyneon™ PVDF 6010/0000 is an extrusion or compression molding grade homopolymer, ideal for pipes, tubes, sheets, and slabs. PVDF is inherently pure and chemically resistant to a wide array of aggressive media. This grade exhibits excellent thermal and dimensional stability, high strength, and maintains its mechanical properties at elevated temperatures.Excellent chemical resistance to a wide variety of aggressive fluids and solventsGood permeation resistanceExcellent strength and dimensional stabilityExtrusion or compression molding gradeGood color stabilityInformation provided by Dyneon, A 3M Company
Physical Properties Metric English Comments
Density 1.78 g/cc
0.0643 lb/in³
ISO 1183
Water Absorption <= 0.040 %
<= 0.040 %
24 hr @ 23°C; ISO 62 (method 1)
Melt Index of Compound 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
6.0 g/10 min

@Load 5.00 kg,
Temperature 230 °C
6.0 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 42.0 MPa
6090 psi
50mm/min; ASTM D638
Tensile Strength, Yield 55.0 MPa
7980 psi
50mm/min; ASTM D638
Elongation at Break 35 %
35 %
50mm/min; ASTM D638
Elongation at Yield 7.0 %
7.0 %
50mm/min; ASTM D638
Flexural Modulus 2.10 GPa
305 ksi
2mm/min; ASTM D790
Thermal Properties Metric English Comments
Melting Point 173 °C
343 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
Flammability, UL94 V-0
V-0
Oxygen Index 44 %

@Thickness 3.00 mm
44 %

@Thickness 0.118 in
Sheet; ASTM D2863
Descriptive Properties Value Comments
Form Powder