A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Rotational Molding Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and ESCR tests were performed on compression molded samples. Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 0.942 g/cc
0.942 g/cc
ASTM D792
ESCR 100% Igepal® >= 500 hour
>= 500 hour
ASTM D1693
Melt Index of Compound 6.0 g/10 min
6.0 g/10 min
2.16/190; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 17.9 MPa
2600 psi
2"/min; ASTM D638
Elongation at Break 400 %
400 %
2"/min; ASTM D638
Flexural Modulus 0.724 GPa
105 ksi
at 1% secant modulus; ASTM D790
Impact Test 56.9 J

@Thickness 3.17 mm,
Temperature -40.0 °C
42.0 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
ARM impact
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 52.0 °C
126 °F
ASTM D648
Descriptive Properties Value Comments
UV Stabilization UV-8