ACC QSil 12 QSI Quantum Silicones Clear Low Viscosity for Potting Material

Category Polymer , Thermoset , Silicone
Manufacturer Amber Chemical Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ACC QSil 12 QSI Quantum Silicones Clear Low Viscosity for Potting Material.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
QSil 12 is a clear, transparent, low viscosity, two-component, liquid silicone material which cures at room temperature and is primarily intended for potting applications. This material is typically mixed at a ratio of 100:5. Once mixed, the material is self-leveling and will have a useful worklife of approximately two hours. The material will be fully cured after 24 - 48 hours at room temperature. This material can also be vulcanized at elevated temperatures (up to 70°C) to increase the cure speed.Key Features: Low viscosity Variable cure speed, with mild heat Transparency Room temperature cure Good adhesion with use of a primerPart of the Amber Chemical Group. Data provided by manufacturer.
Physical Properties Metric English Comments
Specific Gravity 0.850 g/cc
0.850 g/cc
QSil 12C
1.00 g/cc
1.00 g/cc
cured with 5% curing agent
1.00 g/cc
1.00 g/cc
QSil 12
Viscosity 15 cP
15 cP
QSil 12C
1400 cP
1400 cP
QSil 12
Storage Temperature <= 38.0 °C
<= 100 °F
6 months
Mechanical Properties Metric English Comments
Hardness, Shore A 12
12
cured with 5 % curing agent, 24 hours
18
18
cured with 5% curing agent, 72 hours
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 204 °C
399 °F
Minimum Service Temperature, Air -55.0 °C
-67.0 °F
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
clear; thickness not quantified
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
Dielectric Constant 3.0

@Frequency 1000 Hz
3.0

@Frequency 1000 Hz
Dielectric Strength 15.7 kV/mm
400 kV/in
Dissipation Factor 0.0010

@Frequency 1000 Hz
0.0010

@Frequency 1000 Hz
Processing Properties Metric English Comments
Gel Time 60.0 - 180 min
60.0 - 180 min
Descriptive Properties Value Comments
Color Clear, Slight Haze
QSil 12
Clear, Slight Yellow
QSil 12C