Arkema Group Rilsamid® PA 12 AESNO MED Nylon 12

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer Arkema
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsamid® PA 12 AESNO MED Nylon 12.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rilsamid® AESNO MED is a rigid polyamide 12 with high viscosity designed for tube extrusion. This grade dedicated to extrusion offers the highest quality and it is specifically designed to meet the stringent requirements of the medical applications such as minimally invasive devices. Upon request letters regarding USP Class VI compliance can be provided.Designation: PA12, EHL, 22-010Information provided by Arkema Group
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
ISO 1183
Water Absorption 0.90 %

@Temperature 23.0 °C,
Time 86400 sec
0.90 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 0.70 %

@Temperature 20.0 °C
0.70 %

@Temperature 68.0 °F
50% RH; ISO 62
Mechanical Properties Metric English Comments
Hardness, Shore D 69
69
After 15 sec, Conditioned 15 days at 23°C - 50% RH; ISO 868
75
75
Instantaneous, Conditioned 15 days at 23°C - 50% RH; ISO 868
Tensile Strength at Break 50.0 MPa
7250 psi
Conditioned 15 days at 23°C - 50% RH; ISO 527
Tensile Strength, Yield 43.0 MPa
6240 psi
Conditioned 15 days at 23°C - 50% RH; ISO 527
Elongation at Break <= 200 %
<= 200 %
Conditioned 15 days at 23°C - 50% RH; ISO 527
Elongation at Yield 5.0 %
5.0 %
Conditioned 15 days at 23°C - 50% RH; ISO 527
Tensile Modulus 1.44 GPa
209 ksi
Conditioned 15 days at 23°C - 50% RH; ISO 527
Flexural Modulus 1.18 GPa
171 ksi
Conditioned 15 days at 23°C - 50% RH; ISO 178
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179
1.10 J/cm²

@Temperature 23.0 °C
5.23 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 180 °C
356 °F
ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 130 °C
266 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
ISO 75
Processing Properties Metric English Comments
Processing Temperature 230 - 270 °C
446 - 518 °F
Extrusion Range
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Descriptive Properties Value Comments
Extrusion Temperature 240°C
Recommended