Asahi Kasei Leona® 54G43 43% Glass Filled Nylon 66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer Asahi Kasei
Trade Name Leona®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Asahi Kasei Leona® 54G43 43% Glass Filled Nylon 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Enhanced strength, stiffness, and impact resistance; with 43% GF. Excellent appearance. Applications:Fans, railroad tie insulators, office furniture Information provided by Asahi Kasei
Physical Properties Metric English Comments
Specific Gravity 1.50 g/cc
1.50 g/cc
Dry; ASTM D792
Water Absorption 1.6 %
1.6 %
Wet
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
Dry; ASTM D2863
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
Dry; ASTM D2863
Mechanical Properties Metric English Comments
Hardness, Rockwell M 93
93
Dry; ASTM D785
Hardness, Rockwell R 118
118
Dry; ASTM D785
Tensile Strength, Yield 132 MPa
19100 psi
Wet; ASTM D638
186 MPa
27000 psi
Dry; ASTM D638
Elongation at Break 3.0 %
3.0 %
Dry; ASTM D638
4.0 %
4.0 %
Wet; ASTM D638
Flexural Strength 177 MPa
25700 psi
Wet; ASTM D790
304 MPa
44100 psi
Dry; ASTM D790
Flexural Modulus 5.90 GPa
856 ksi
Wet; ASTM D790
11.0 GPa
1600 ksi
Dry; ASTM D790
Izod Impact, Notched 1.47 J/cm
2.75 ft-lb/in
Dry; ASTM D256
2.26 J/cm
4.23 ft-lb/in
Wet; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
Dry; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
Dry; ASTM D648
Flammability, UL94 HB
HB
Dry