BASF Ultramid® 8260 40% Mineral Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8260 40% Mineral Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8260 is a 40% mineral reinforced PA6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low warp and resistance to sink-mark formation. It is also available in heat stabilized (Ultramid 8260 HS) versions. It can be painted or chrome plated and is also available in pigmented versions.
Physical Properties Metric English Comments
Density 1.291 g/cc
0.04664 lb/in³
Melt; ISO 1183
1.49 g/cc
0.0538 lb/in³
ISO 1183
Water Absorption 1.1 %
1.1 %
24 hour; ISO Test
5.7 %
5.7 %
ISO 62
Moisture Absorption at Equilibrium 1.6 %
1.6 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ASTM Test
Tensile Strength at Break 90.0 MPa
13100 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 85.0 MPa
12300 psi
5mm/min; ISO 527
Elongation at Break 10 %
10 %
5mm/min; ISO 527
10 %
10 %
0.2 in/min; ASTM Test
Tensile Modulus 6.40 GPa
928 ksi
1mm/min; ISO 527
0.970 GPa

@Temperature 120 °C
141 ksi

@Temperature 248 °F
ISO Data
1.36 GPa

@Temperature 80.0 °C
197 ksi

@Temperature 176 °F
ISO Data
8.31 GPa

@Temperature -40.0 °C
1210 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 138 MPa
20000 psi
ASTM Test
140 MPa
20300 psi
ISO Data
34.0 MPa

@Temperature 120 °C
4930 psi

@Temperature 248 °F
ASTM Test
35.0 MPa

@Temperature 93.0 °C
5080 psi

@Temperature 199 °F
ASTM Test
55.0 MPa

@Temperature 65.0 °C
7980 psi

@Temperature 149 °F
ASTM Test
207 MPa

@Temperature -40.0 °C
30000 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 5.20 GPa
754 ksi
ISO Data
5.76 GPa
835 ksi
ASTM Test
0.810 GPa

@Temperature 93.0 °C
117 ksi

@Temperature 199 °F
ASTM Test
0.815 GPa

@Temperature 120 °C
118 ksi

@Temperature 248 °F
ASTM Test
1.54 GPa

@Temperature 65.0 °C
223 ksi

@Temperature 149 °F
ASTM Test
Izod Impact, Notched 0.530 J/cm

@Thickness 3.17 mm
0.993 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Unnotched 16.4 J/cm
30.7 ft-lb/in
ASTM Test
Charpy Impact Unnotched 11.5 J/cm²
54.7 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
ISO 179
0.300 J/cm²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 50.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
27.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
CTE, linear, Parallel to Flow 46.0 µm/m-°C
25.6 µin/in-°F
ISO 11359
CTE, linear, Transverse to Flow 58.0 µm/m-°C
32.2 µin/in-°F
ISO 11359
Specific Heat Capacity 1.999 J/g-°C
0.4778 BTU/lb-°F
Melt
Thermal Conductivity 0.281 W/m-K
1.95 BTU-in/hr-ft²-°F
Melt
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 195 °C
383 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 125 °C
257 °F
ASTM Test
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Processing Properties Metric English Comments
Melt Temperature 275 °C
527 °F
Injection molding
Mold Temperature 95.0 °C
203 °F
Injection molding
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic X