BASF Ultramid® KR 4350 PA6/6T (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® KR 4350 PA6/6T (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: For injection-molding and extrusion, exhibiting high toughness, strength and stiffness, low water absorption, high melting point (295 °C [563°F]). The mechanical properties remain constant after moisture absorption up to a temperature of 60°C [140°F].Information provided by BASF
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
ISO 1183
Water Absorption 6.5 - 7.5 %
6.5 - 7.5 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 1.6 - 2.0 %
1.6 - 2.0 %
23°C; 50% RH; ISO 62
Viscosity Measurement 130
130
ISO 307
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
restricted
Mechanical Properties Metric English Comments
Tensile Strength, Yield 90.0 MPa
13100 psi
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 3.20 GPa
464 ksi
ISO 527-1/-2
Tensile Creep Modulus, 1000 hours 2300 MPa

@Strain <=0.500 %
334000 psi

@Strain <=0.500 %
ISO 899-1
Thermal Properties Metric English Comments
Specific Heat Capacity 1.50 J/g-°C
0.359 BTU/lb-°F
Thermal Conductivity 0.230 W/m-K
1.60 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 295 °C
563 °F
DIN 53765
Maximum Service Temperature, Air 110 °C
230 °F
for 50% loss of tensile strength after 20000hr
130 °C
266 °F
for 50% loss of tensile strength after 5000hr
250 °C
482 °F
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Constant 4.0

@Frequency 1.00 Hz
4.0

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.040

@Frequency 1.00e+6 Hz
0.040

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 310 - 330 °C
590 - 626 °F
Injection-molding/Extrusion
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Injection-molding
Descriptive Properties Value Comments
Commercial Status Europe