Beijing Chemical Industry KAIFA® S-206 PPS Resin
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® S-206 PPS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass fiber reinforced and mineral filledInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | 0.60 % | 0.60 % | ASTM D638 |
| Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
| Flexural Modulus | 1.50 GPa | 218 ksi | ASTM D790 |
| Charpy Impact Unnotched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 0.650 J/cm² | 3.09 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.5 @Frequency 1e+6 Hz |
4.5 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 15.0 kV/mm @Thickness 2.00 mm |
381 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.0081 @Frequency 1e+6 Hz |
0.0081 @Frequency 1e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 280 - 315 °C | 536 - 599 °F | Injection Temp. |
| Mold Temperature | 135 - 150 °C | 275 - 302 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 60.0 MPa | 8700 psi |
Users viewing this material also viewed the following:
- Resinlab® CYNERGY CA6502 Adhesive
- Materion BrushBronze® 630 (AMS 4640) 1.0" - 2.0"
- Teknor Apex APEX® 80-C118Q Polyvinyl Chloride, Flexible
- Styron DL 238NA Carboxylated SB
- Teknor Apex Flexalloy® 9605-70FR Polyvinyl Chloride, Elastomer
- A. Schulman PP 3353-01 Polypropylene Medium Impact Polypropylene
- DSM Stanyl® TW271F6 Nylon 46-30% Glass Reinforced (European and Asian Grade) (Dry)
- Eurostar Staramide BG2ST43 PA6, Glass Fiber Filled, Impact Modified, Injection Molded
- Eurotec® Tecomid® NB40 GR20 NL XA60 PA6, 20% glass fiber reinforced, flame retardant - halogen & red phosphorus free, heat stabilized, natural
- 3M Scotch-Weld™ DP-5106 Control Joint Sealant
Copyright © lookpolymers.com All Rights Reserved