Borealis Bormod™ HC905TF Polypropylene Homopolymer for Thermoforming

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer Borealis
Trade Name Bormod™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Bormod™ HC905TF Polypropylene Homopolymer for Thermoforming.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Bormod HC905TF is a low melt flow rate polypropylene homopolymer intended for thermoformed packaging applications. This homopolymer is produced using the Borealis Controlled Crystallinity Polypropylene (CCPP) technology. This provides a polypropylene with excellent processing consistency and its high crystallization temperature allows for reduced cycle time and increased output. Bormod HC905TF is suitable for both in-line and off-line thermoforming where it shows a wide processing window and gives very consistent shrinkage behavior after forming.Bormod HC905TF is recommended for the following applications including highly transparent trays, cups and containers, houseware and thin wall packaging, margarine tubs and dairy containers, and blending with copolymers for lids.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 0.905 g/cc
0.0327 lb/in³
ISO 1183
Linear Mold Shrinkage 0.015 - 0.020 cm/cm
0.015 - 0.020 in/in
Melt Flow 2.8 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.8 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 39.50 MPa
5729 psi
At 50 mm/min; ISO 527-2
Elongation at Yield 7.0 %
7.0 %
At 50 mm/min; ISO 527-2
Tensile Modulus 2.10 GPa
305 ksi
At 1 mm/min; ISO 527-2
Flexural Modulus 2.00 GPa
290 ksi
At 2 mm/min; ISO 178
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 164 - 168 °C
327 - 334 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 118 °C
244 °F
ISO 75-2
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Processing Properties Metric English Comments
Melt Temperature 210 - 240 °C
410 - 464 °F
Mold Temperature 20.0 - 40.0 °C
68.0 - 104 °F