Borealis Xmod™ GD302HP Polypropylene, Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler
Manufacturer Borealis
Trade Name Xmod™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Xmod™ GD302HP Polypropylene, Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Xmod™ GD302HP is a 30 % chemically coupled high performance glass fiber reinforced polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and is easy to process. Applications: dashboard carriers, door module carriers, and structural seat parts.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
ISO 1183
Linear Mold Shrinkage 0.00060 cm/cm
0.00060 in/in
average process; in flow; 150x80x2mm
0.00080 cm/cm
0.00080 in/in
average process; cross flow; 150x80x2mm
Melt Flow 3.3 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.3 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 65.0 MPa
9430 psi
ISO 527-2
Elongation at Yield 4.0 %
4.0 %
ISO 527-2
Tensile Modulus 5.60 GPa
812 ksi
1mm/min; ISO 527-2
Flexural Strength 86.0 MPa
12500 psi
ISO 178
Flexural Modulus 5.10 GPa
740 ksi
2mm/min; ISO 178
Izod Impact, Notched (ISO) 16.0 kJ/m²

@Temperature -20.0 °C
7.61 ft-lb/in²

@Temperature -4.00 °F
ISO 180/1A
28.0 kJ/m²

@Temperature 23.0 °C
13.3 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -20.0 °C
28.6 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
6.50 J/cm²

@Temperature 23.0 °C
30.9 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 1.30 J/cm²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
2.40 J/cm²

@Temperature 23.0 °C
11.4 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 132 °C
270 °F
ISO 75-2
Processing Properties Metric English Comments
Processing Temperature 230 - 280 °C
446 - 536 °F
mass temperature
Feed Temperature 40.0 - 80.0 °C
104 - 176 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec
3.94 - 7.87 in/sec
Hold Pressure 30.0 - 60.0 MPa
4350 - 8700 psi
Descriptive Properties Value Comments
Back Pressure as low as possible
Screw Speed low to medium