CENTROPLAST CENTROMID 6.6 CF 20 Polyamide 6.6 carbon fiber

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Carbon Fiber Filled
Manufacturer CENTROPLAST Engineering Plastics GMBH
Trade Name CENTROMID
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CENTROPLAST CENTROMID 6.6 CF 20 Polyamide 6.6 carbon fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This material has very high strength and a high operating temperature. It can be used for precision components, drive parts and housings.Information provided by CENTROPLAST Engineering Plastics GMBH
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 2.2 %
2.2 %
in normal climate 23°C/50%RH; ISO 62
Water Absorption at Saturation 6.5 %
6.5 %
in water at 23°C; ISO 62
Mechanical Properties Metric English Comments
Ball Indentation Hardness 240 MPa
34800 psi
value at 30 sec.; ISO 2039-1
Tensile Strength, Yield 230 MPa
33400 psi
v = 50 mm/min; ISO 527-2
Elongation at Break 2.5 %
2.5 %
ISO 527-2
Tensile Modulus 17.0 GPa
2470 ksi
ISO 527-2
Flexural Modulus 14.0 GPa
2030 ksi
ISO 178
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 25.0 µm/m-°C

@Temperature 20.0 °C
13.9 µin/in-°F

@Temperature 68.0 °F
ISO 11359
Thermal Conductivity 0.430 W/m-K
2.98 BTU-in/hr-ft²-°F
Melting Point 260 °C
500 °F
10K/min; ISO 3146
Maximum Service Temperature, Air 180 °C
356 °F
Long Term
240 °C
464 °F
Short term
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
ISO 75-2
Flammability, UL94 HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
HB

@Thickness 6.00 mm
HB

@Thickness 0.236 in