- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 473 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 473 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ASTM D648 |
| Niche Polymer PA66GM38BK Nylon 66, 38% Glass/Mineral Fiber Filled Information provided by Niche Polymer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75/2Af |
| Radici Radilon® ARV300 RKC (dry) Nylon 66 Glass-fiber reinforced with heat and hydrolysis resistanceInformation provided by Radici group. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | Unannealed; ISO 75-2 |
| PolyOne Nymax™ GF 1200 A 55 HS Natural Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75 |
| Nilit FRIANYL A63 CV10 Nylon 6.6 for injection molding, 10% carbon fiber reinforced Nylon 6.6 for injection molding (good conductive and electrostatic properties).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| Lehmann & Voss LUVOCOM® 1-1114 Polyamide 66, with carbon fiber, low-warpage, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Stiff parts, low coefficient of expansion, low viscose, anisotropic.Reduced moment of inertia c.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| Lehmann & Voss LUVOCOM® 1-7882 Polyamide 66, with carbon fiber and PTFE, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Electrically conductive, suita.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| Lehmann & Voss LUVOCOM® 1/CF/15/HS Polyamide 66, with carbon fiber, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia comp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| Lehmann & Voss LUVOCOM® 1/CF/30/TF/15 Polyamide 66, with carbon fiber and PTFE, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Improved friction and wear beh.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| Lehmann & Voss LUVOCOM® 1/GF/30/TF/15/HS-B Polyamide 66, with glass fiber and PTFE, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Heat stabilised.High dimension.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| Lehmann & Voss LUVOCOM® 1-0866 Polyamide 66, with aramid reinforcement, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Low warpage.Improved heat resistance.Control disks, cams, sliding elements and other duty parts.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| LATI Latamid 66 H2 G/25 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termop.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| LATI Latamid 66 VH G/30 PA 66, 30% Glass Fiber Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Hydrolysis stabilized. Glycol stabilized. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInfo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| LATI Laticonther 80 CPG/700 PPS, Glass Fiber Reinforced High thermal conductivity product based on Polyphenylene Sulfide (PPS). Special filler. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ASTM D648 |
| Solvay TECHNYL® A 218 V25 NAT BA PA66, 25% glass fiber, DRY Description: Polyamide 66, reinforced with 25% of glass fiber, specially stabilized to improve its resistance to oils and greases, for injection molding.Available in: Asia PacificProduct Application.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C @Thickness 3.20 mm |
473 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON Valox_VCF2020 PET LNP* Stat-kon* Valox_VCF2020 compound is a 20% carbon fiber reinforced PET. Conductive applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| Shinil Chemical SHINNANO PA-66 Polymer Nanocomposite Engine Cover SHINNANO is the product line of polymer nanocomposite made by dispersing nano fillers, mainly, NANOCLAY. Recently, Shinil has developed varios nanocomposite grades for automotive applications using.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C @Thickness 3.20 mm |
473 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp RF005 PA 66 (Asia Pacific) LNP* Thermocomp* RF005 is a compound based on Nylon 66 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP RF006S PA6.6 (Europe-Africa-Middle East) LNP* THERMOCOMP* RF006S is a compound based on PA 66 resin containing Glass Fiber. Added features include: Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Sax Polymers SAXAMID 226F5 Nylon 6.6, 25% Glass Fiber SAXAMID 226F5 is a general purpose polyamide 6.6 injection-molding-grade reinforced with 25% glass fibers. It has high mechanical strength in combination with good flow properties.Information provid.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-93 |
| Wellman Wellamid® FRGFT1741-BK2 Nylon 66, 32% Glass Fiber Reinforced, Flame Retardant All information provided by Wellman Engineered Resins. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-93 |
| Wellman Wellamid® GF33-66 XE-BKDX9 33% Glass Fiber Reinforced Nylon 66 Description: Glass Fiber Reinforced Nylon 66Information provided by Wellman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Starflam RF0077E PA66, 35% Glass Filled, Injection Molded Starflam RF0077E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Fiber Reinforced, Polyamide 66 Injection Molding Resin (also known as RF1007Z270)Information provided by Polymer T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ASTM D648 |
| Clariant PA123G30 Nylon 66, 30% Glass Fiber, Impact Modified, Heat Stabilized Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75 |
| Eurotec® Tecomid® NA43 GR25 NL XA43 PA6.6, 25% glass fiber reinforced, flame retardant - red phosphorus free, heat stabilized, natural, UL registered Information provided by Eurotec® |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-2/AF |
| Addiplast Addinyl A2I V25 Flame Retardant Nylon 66, 25% Glass Filled Flame retardant, 25% glass fiber reinforced, halogen freeInformation provided by Addiplast. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1/-2 |
| Celanese Zenite® FG6330 NC011 LCP Zenite® FG6330 NC011 is a 30% mineral reinforced liquid crystal polymer resin with FDA approval for use in repeated food-contact applications.Celenese acquired the Zenite product line from DuPont i.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® GVX-5 H black 9915 PA*-GF50 Product description: Grivory GVX-5H black 9915 is a 50% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic copolyam.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ASTM D648 |
| Chevron Phillips Xtel® XK2240 Polyphenylene Sulfide Alloy
(discontinued **) Natural Color Polyphenylene Sulfide AlloyXtel™ XK2240 is a high performance, glass fiber reinforced, PPS-based alloy developed to provide excellent mechanical strength with an unique blend of tough.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1, -2 |
| Celanese VECTRA MLX4243 LCP High heat resistent, mineral filled LCP material with high flow. Material has silver metallic appearance for use in aesthetic metallic effect applications.Information provided by Celanese |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C @Thickness 3.20 mm |
473 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP VERTON RF-7007 EM HS PA 66 (Asia Pacific) LNP VERTON* RF-7007 EM HS is a compound based on Nylon 66 resin containing Long Glass. Added features of this material include: Easy Molding. |
|||