Carmel Olefins CARMELTECH™ QB 79 P Polypropylene Random Copolymer for Pressure Pipe

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer	Carmel Olefins
Trade Name	CARMELTECH™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Carmel Olefins CARMELTECH™ QB 79 P Polypropylene Random Copolymer for Pressure Pipe.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

CARMELTECH™ QB 79 P is a high molecular weight, low melt flow rate polypropylene random copolymer, especially designed for extrusion of pressure pipes and injection molding of fittings. This grade offers a combination of ease of processing and excellent mechanical properties. It has been formulated for long term heat stabilization and good resistance to extraction by hot water and detergents. APPLICATIONS CARMELTECH™ QB 79 P is suitable for in-house hot and cold water pipes and fittings, floor and wall heating systems, radiator connections, and industrial applications.

Physical Properties	Metric	English	Comments
Melt Flow	0.28 g/10 min @Load 2.16 kg, Temperature 230 °C	0.28 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
	0.50 g/10 min @Load 5.00 kg, Temperature 190 °C	0.50 g/10 min @Load 11.0 lb, Temperature 374 °F	ASTM D1238
	1.2 g/10 min @Load 5.00 kg, Temperature 230 °C	1.2 g/10 min @Load 11.0 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	23.0 MPa	3340 psi	ASTM D638
Elongation at Yield	13 %	13 %	ASTM D638
Flexural Modulus	0.950 GPa	138 ksi	ASTM D790
Izod Impact, Notched	0.850 J/cm @Temperature >=0.000 °C	1.59 ft-lb/in @Temperature >=32.0 °F	ASTM D256
	3.00 J/cm @Temperature >=23.0 °C	5.62 ft-lb/in @Temperature >=73.4 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	85.0 °C	185 °F	ASTM D648
Vicat Softening Point	133 °C @Load 1.02 kg	271 °F @Load 2.25 lb	ASTM D1525