Chevron Phillips HiD® 9632 HDPE Blown Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips HiD® 9632 HDPE Blown Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics: Copolymerization Enhances Film Toughness, Excellent Film Drawdown Ideally Suited for Thin Films Production, Lower Melt Index (Higher Molecular Weight) Results in Increased Film Strength, Unique Molecular Architecture Gives Moisture Barrier Properties Typical of Much Higher Density Resins, Excellent Embossing Properties, Excellent ProcessabilityApplications:Notion and Millinery Bags, Multi-wall Liners, Coextrusions, Can liners. Recommended Die Gap: 0.89 mm.Film properties below based on film thickness of 25.4 µm.Data provided by Chevron Chemical.
Physical Properties Metric English Comments
Density 0.945 g/cc
0.0341 lb/in³
ASTM D1505
Moisture Vapor Transmission 0.160 cc-mm/m²-24hr-atm
0.406 cc-mil/100 in²-24hr-atm
ASTM F1249
Melt Flow 0.17 g/10 min
0.17 g/10 min
Condition E; ASTM D 1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 450 %
450 %
ASTM D882
Film Elongation at Break, TD 600 %
600 %
ASTM D882
Secant Modulus, MD 0.620 GPa
89.9 ksi
ASTM D882
Secant Modulus, TD 0.760 GPa
110 ksi
ASTM D882
Elmendorf Tear Strength, MD 0.591 g/micron
15.0 g/mil
Notched; ASTM D1922
Elmendorf Tear Strength, TD 23.2 g/micron
590 g/mil
ASTM D1922
Dart Drop 3.30 g/micron
83.8 g/mil
1.5 in. dart/26 in. drop height; ASTM D 1709
Film Tensile Strength at Break, MD 55.0 MPa
7980 psi
ASTM D882
Film Tensile Strength at Break, TD 43.0 MPa
6240 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 122 °C
252 °F
ASTM D1525
Processing Properties Metric English Comments
Melt Temperature 221 °C
430 °F