Covestro Bayblend® 2753 Polycarbonate + ABS Blend, Automotive  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® 2753 Polycarbonate + ABS Blend, Automotive  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This product was discontinued prior to the separation.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0070 cm/cm
0.0070 in/in
ASTM D955
Spiral Flow 61.0 cm

@Thickness 2.50 mm
24.0 in

@Thickness 0.0984 in
at 254°C melt temp.
Mechanical Properties Metric English Comments
Hardness, Rockwell R 113
113
ASTM D785
Tensile Strength, Yield 51.0 MPa
7400 psi
ASTM D638
Elongation at Break 56 %
56 %
ASTM D638
Tensile Modulus 2.50 GPa
363 ksi
ASTM D638
Flexural Yield Strength 85.0 MPa
12300 psi
ASTM D790
Flexural Modulus 2.34 GPa
339 ksi
ASTM D790
Izod Impact, Notched 2.50 J/cm

@Temperature -40.0 °C
4.68 ft-lb/in

@Temperature -40.0 °F
ASTM D256
6.90 J/cm

@Thickness 3.17 mm
12.9 ft-lb/in

@Thickness 0.125 in
ASTM D256
Impact Test 41.0 J

@Thickness 2.50 mm
30.2 ft-lb

@Thickness 0.0984 in
Instrumented Impact, Total Energy; 7.6 mph, 3 in. clamp, 0.5 in. dart; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 115 °C

@Thickness 3.20 mm
239 °F

@Thickness 0.126 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C

@Thickness 3.17 mm
207 °F

@Thickness 0.125 in
ASTM D648
Vicat Softening Point 110 °C
230 °F
Rate B; ISO 306
UL RTI, Electrical 85.0 °C

@Thickness 1.57 mm
185 °F

@Thickness 0.0618 in
UL RTI, Mechanical with Impact 85.0 °C

@Thickness 1.57 mm
185 °F

@Thickness 0.0618 in
UL RTI, Mechanical without Impact 85.0 °C

@Thickness 1.57 mm
185 °F

@Thickness 0.0618 in
Flammability, UL94 HB

@Thickness 1.57 mm
HB

@Thickness 0.0618 in
HB

@Thickness 1.57 mm
HB

@Thickness 0.0618 in
Electrical Properties Metric English Comments
Comparative Tracking Index 175 V
175 V
IEC 112