Eastman E6838-913P Polyethylene  (discontinued **)

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman E6838-913P Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyethylene E6838-913P natural is a specialty formulation suggested for high-speed extrusion coating applications. E6838-913P offers improvements over standard low-density polyethylene in adhesion to foil.Applications/UsesFoilEastman Chemical Company sold its polyethylene business to Westlake Chemical Corporation in Dec. 2006. This grade no longer appears in the Westlake product line.
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
ASTM D4883
Melt Flow 4.9 g/10 min

@Load 2.16 kg,
Temperature 190 °C
4.9 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 9.00 MPa
1310 psi
500 mm/min; ASTM D638
Tensile Strength, Yield 12.4 MPa
1800 psi
500 mm/min; ASTM D638
Elongation at Break 150 %
150 %
500 mm/min; ASTM D638
Flexural Modulus 0.283 GPa
41.0 ksi
2% Secant, 12.7 mm/min; ASTM D790
Thermal Properties Metric English Comments
Vicat Softening Point 92.0 °C
198 °F
ASTM D1525
Brittleness Temperature -68.0 °C
-90.4 °F
ASTM D746
Descriptive Properties Value Comments
Process Film