Entec Hylox® 9015 PBT, 15% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer Entec Engineered Resins
Trade Name Hylox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Entec Hylox® 9015 PBT, 15% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Entec.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ASTM D792
Water Absorption 0.070 %
0.070 %
24 hrs; ASTM D570
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
0.125 in; ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90
90
ASTM D785
Tensile Strength at Break 93.1 MPa
13500 psi
ASTM D638
Elongation at Break 4.0 %
4.0 %
ASTM D638
Flexural Strength 148 MPa
21400 psi
ASTM D790
Flexural Modulus 4.83 GPa
700 ksi
ASTM D790
Izod Impact, Notched 0.587 J/cm
1.10 ft-lb/in
73°F; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 50.4 µm/m-°C

@Temperature 20.0 °C
28.0 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Unannealed; ASTM D648
Flammability, UL94 HB
HB
0.0280 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Constant 3.6

@Frequency 100 Hz
3.6

@Frequency 100 Hz
ASTM D150
Dielectric Strength 26.0 kV/mm
660 kV/in
ASTM D149
Processing Properties Metric English Comments
Rear Barrel Temperature 232 - 243 °C
450 - 470 °F
Middle Barrel Temperature 238 - 249 °C
460 - 480 °F
Front Barrel Temperature 243 - 254 °C
470 - 490 °F
Nozzle Temperature 243 - 254 °C
470 - 490 °F
Melt Temperature 249 - 260 °C
480 - 500 °F
Mold Temperature 82.2 - 121 °C
180 - 250 °F
Drying Temperature 121 °C
250 °F
Dry Time <= 12 hour
<= 12 hour
Moisture Content <= 0.020 %
<= 0.020 %
Injection Pressure 6.89 - 11.7 MPa
1000 - 1700 psi
Back Pressure 0.138 - 0.414 MPa
20.0 - 60.0 psi
Shot Size 40 - 80 %
40 - 80 %
Screw Speed 40 - 80 rpm
40 - 80 rpm
Descriptive Properties Value Comments
Holding Pressure 500 to 900 psi
Injection Rate Moderate-Fast